| 牌号简介 About |
|---|
| ADIPRENE L 325是一种基于聚醚的、TDI端接的液态聚氨酯预聚物，可通过传统的手工和机械混合技术轻松加工。当与4，4’-亚甲基双（2-氯苯胺）固化时，这一阿迪普林L家族成员生产的70-75邵尔D硬度范围内的高品质硫化胶。这些坚韧、高弹性的弹性体具有许多独特的特点：优异的低温柔韧性、优异的耐磨性、良好的水解稳定性、低压缩永久变形的Adiprene L 325在与防腐剂混合时比Adiprene L 315具有更长的工作寿命，因此更适用于大型零件的制备。 ADIPRENE L 325 is a polyether-based, TDI terminated liquid urethane prepolymer that is readily processable by conventional hand and machine mixing techniques. When cured with 4,4'-methylene-bis(2-chloroaniline), this member of the ADIPRENE L family produces high quality vulcanizates in the 70-75 Shore D hardness range. These tough, highly resilient elastomers have many unique features: Excellent low-temperature flexibility Excellent abrasion resistance Good hydrolytic stability Low compression set ADIPRENE L 325 gives a longer working life when mixed with curatives than does ADIPRENE L 315, so it is more suitable for the preparation of large parts. |
产品描述 Product Description
加工条件：浇铸 casting
性能特点： 耐磨; 耐低温柔性; 尺寸稳定性好; 耐水解; 有弹性; 韧性好; Good flexibility,Good Dimensional Stability,Hydrolysis stability,Elastic,Low temperature toughness,Good wear resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
60.7 | MPa | ASTM D412 |
|
100% 应变 100% strain |
25.9 | MPa | ASTM D412 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
260 | % | ASTM D412 |
|
撕裂强度 tear strength |
|||
|
开裂 cracking |
20 | kN/m | ASTM D470 |
|
压缩形变 Compression deformation |
|||
|
70℃，22 hr 70℃，22 hr |
% | ASTM D395A | |
|
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 friction coefficient |
|||
|
NBS NBS |
|||
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
固化时间 Curing time |
|||
|
100℃ 100℃ |
hr | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ASTM D2240 | ||
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
热变形温度 Hot deformation temperature |
℃ | ||
|
热固组件 Thermosetting components |
|||
|
树脂 resin |
|||
|
硬化法 Hardening method |
|||
|
储存稳定性 storage stability |
min | ||
|
后固化时间 Post curing time |
|||
|
100℃ 100℃ |
hr | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
高桥石化ABS产品 获医用领域客户好评
2022-01-20 搜料网资讯： 日前，高桥石化首次产出10吨医用定制化ABS产品，客户使用后反馈良好。这是该公司ABS产品首次进入医用市场。 此前，高桥石化了解到某医疗器械企业需求后，立即对ABS产 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付