ULTEM™HU1010树脂透明,增强流动聚醚酰亚胺(Tg 217C)。 符合ECO。 用于医疗设备和制药应用。 变更的医疗保健管理,生物相容性(ISO 10993或USP VI级),符合食品接触。 可用EtO和蒸汽灭菌。 Transparent, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI); food contact compliant; Steam, Gamma, EtO; and E-beam sterilizable. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
337℃,6.6kg 337℃,6.6kg |
18 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
360℃,5 kg 360℃,5 kg |
25.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.5~0.7 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
1.3 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/5 | |
屈服 yield |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
50 mm跨距 50 mm span |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
屈服,50 mm跨度 Yield, 50 mm span |
MPa | ASTM D790 | |
屈服,100 mm跨度 Yield, 100 mm span |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
落镖冲击(23℃) Dart impact (23 ℃) |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
1.6 mm,在空气中 1.6 mm in air |
kV/mm | ASTM D149 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
ASTM D150 | ||
2.45 GHz 2.45 GHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率(HVTR) High voltage arc marking rate (HVTR) |
UL 746 | ||
热丝引燃(HWI) Hot wire ignition (HWI) |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.71 mm 0.71 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
NBS烟雾密度 NBS smoke density |
|||
Flaming,Ds,4 min Flaming,Ds,4 min |
ASTM E662 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
我国钛白粉市场供需趋紧或常态
2017-10-24 据前瞻产业研究院发布的《钛白粉行业市场需求分析报告》分析表明,2017年和2018年钛白粉国内需求增速将分别为10%和8%,即2017年国内需求新增21万吨(涂料15万吨、塑料3万吨、造纸3万吨),2018年国内需求新增18万吨(涂料12万吨、塑料3万吨、造纸3万吨)。需求增速高于产能增速使得钛白粉行业的供需平衡进一步趋紧。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |