| 牌号简介 About |
|---|
| Promyde® B30 P2 G30 U0。注模聚酰胺6与30%的玻璃纤维，阻燃剂使用卤素和红磷无阻燃系统。特性Promyde® B30 P2 G30 U0是一种具有30%玻璃纤维的聚酰胺6，具有高机械强度、热稳定和注模润滑。它的卤素和红磷无阻燃系统提高其阻燃性能到v0-ul级。应用Promyde® B30 P2 G30 U0允许快速和高效的模具填充和容易的模具释放，结合其优良的机械性能和阻燃性能，使其适用于电气和电子工业中特殊使用的组件。 Promyde B30 P2 G30 U0. Injection Moulding Polyamide 6 with 30% glass fibre, and flame retardant using a halogen and red phosphorous free flame retardant system. CHARACTERISTICS Promyde B30 P2 G30 U0 is a polyamide 6 with 30% glass fibre with high mechanical strength, heat stabilized and lubricated for injection moulding. Its halogens and red-phosphorous free flame retardant system enhances its flame behavior to V0- UL rated category. APPLICATIONS Promyde B30 P2 G30 U0 allows a fast and efficient mould filling, and an easy mould release, that combined with its excellent mechanical properties, and its flame retardant properties make it suitable for components specially used in electrical and electronics industries. |
产品描述 Product Description
用途：电气元件;电气/电子应用领域;
加工条件：注射成型 Injection Molding
性能特点： 无卤; 机械强度好; 热稳定性好; 含脱模剂; 成型周期快; 低磷含量; 润滑性; 阻燃; 易加工; Good Rigidity,Excellent Processability,Quick molding cycle,Halogen free,Good stripping performance,Flame Characteristics,Lubricating,Low to no phosphorus content,Heat Stabilized
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.40 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.20-0.50 | % | ISO 294-4 |
|
TD TD |
0.70-0.90 | % | ISO 294-4 |
|
粘度测定 Viscosity measurement |
125 | ISO 307 | |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
6.5 | % | ISO 62 |
|
23℃，50% RH 23℃，50% RH |
% | ISO 62 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ISO 75-2/Af | |
|
熔化温度 Melting temperature |
℃ | ISO 3146 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ISO 11359-2 | |
|
TD TD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻 Volumetric resistance |
Ω.cm | IEC 60093 | |
|
表面电阻 Surface resistance |
Ω.cm | IEC 60093 | |
|
介电常数 Dielectric constant |
|||
|
|
1 MHz | IEC 60250 | |
|
耗散因数 Dissipation factor |
|||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
|
V-0 | UL 94 | |
|
|
V-0 | UL 94 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0,005 g/ml H2SO4 |
| 3 0.079 in/min |
| 4 10°C/min |
|
【新闻资讯】查看全部
北美聚氨酯泡沫出现增长
2015-11-27 北美聚氨酯泡沫市场复合年均增长率有望拉涨6%至2020年。聚氨酯材料生产遍及整个北美地区，其中美国占生产的60%以上。 增长主要体现在住宅及工业中喷涂聚氨酯泡沫应用，美军在中东地区的军事基地中隔离帐篷及其他应用等。聚氨酯也被用于有效的伤口敷料，制药传递媒质，可靠的药物输送，舒适的助行器及卫生的医疗环境等方面。 聚氨酯泡沫还被广泛用于消费品生产，它们舒适耐用，轻质便宜，因而成为许多行业的首选。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付