| 牌号简介 About |
|---|
| 符合ISO 1043-1的材料规范：聚丙烯，含30%重量的灰份，长玻璃纤维增强。抗冲击改性共聚物。纤维与聚丙烯基体发生化学耦合。球是圆柱形的，通常也包括10 mm长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架，因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型，可以制造出具有高再现性的复杂零件。应用领域：汽车功能/结构件 Material code according to ISO 1043-1: PP Polypropylene with 30 weight percent ash content, long glass fibers reinforced. Impact modified, copolymer. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
产品描述 Product Description
用途：汽车领域的应用;
加工条件：注射成型 Injection Molding
性能特点： 化学耦合; 机械强度好; 共聚物; 耐低温冲击; 低翘曲性; 冲击性能好; 韧性好; Good Rigidity,Low warping,Good flexibility,High impact resistance,Chemical coupling,Copolymer,low-temperature impact resistance
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.13 | g/cm³ | ISO 1183 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
-- -- |
6000 | MPa | ISO 527-2/1A/1 |
|
80℃ 80℃ |
4100 | MPa | ISO 527-2/1A |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
95.0 | MPa | ISO 527-2/1A/5 |
|
80℃ 80℃ |
50.0 | MPa | ISO 527-2/1A |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
断裂，80℃ Fracture, 80 ℃ |
% | ISO 527-2/1A | |
|
弯曲模量 Bending modulus |
ISO 178 | ||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
80℃ 80℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
ISO 178 | ||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
80℃ 80℃ |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 10°C/min |
|
【新闻资讯】查看全部
陶氏德克萨斯州新建丙烷脱氢(PDH)装置已投产
2015-12-29 美国陶氏化学位于德克萨斯州的新建丙烷脱氢(PDH)装置已投产运行。该装置采用霍尼韦尔UOP技术，丙烯产能为75万吨/年。 陶氏副主席和首席运营官James R. Fitterling表示“我们在乙烯和丙烯上的集成投资大大减少了第三方购买原材料的成本，促进了陶氏衍生品业务的发展。墨西哥湾岸区的投资将作为强化市场竞争和提高原料结构等长期发展的基础。” 日前，陶氏化学也计划在德克萨斯州自由港完成去瓶颈项目，增加2016年第二季度的甲基丙烯酸缩水甘油酯(GMA)产能 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付