牌号简介 About |
---|
PRE-ELEC® PE 1201是一种基于PE-HD的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除低电阻率外,PRE-ELEC® PE 1201还具有良好的机械性能平衡,易于挤压。典型的应用包括单层压力管(PE 80)的挤压,用于爆炸性环境区域和可焊接或真空成型而无需预干燥的板材。 PRE-ELEC® PE 1201 is a conductive thermoplastic compound based on PE-HD. The electrical conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PE 1201 has an excellent balance of mechanical properties and is easy to extrude. Typical applications include extrusion of monolayer pressure pipes (PE 80) for areas with explosive atmosphere and sheets which can be welded or vacuum formed without pre-drying. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.996 | g/cm³ | ASTM D792 |
密度 Density |
1.00 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
3.0 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
3.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
3.0 to 4.0 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
4 mm 4 mm |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,4 mm Fracture, 4 mm |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
4 mm 4 mm |
MPa | ASTM D790 | |
4 mm 4 mm |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
ISO 180 | ||
Area Area |
ASTM D256 | ||
-20℃,4.00 mm -20℃,4.00 mm |
kJ/m² | ASTM D256 | |
23℃,4.00 mm 23℃,4.00 mm |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
-20℃,4 mm -20℃,4 mm |
ASTM D256 | ||
23℃,4 mm 23℃,4 mm |
ASTM D256 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 2 |
ISO 180 | ||
-20℃ -20℃ |
ISO 180 | ||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 3 | |
-- -- |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ESD STM11.11 | |
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4 mm thickness |
3 标准 B (120°C/h), 载荷2 (50N) |
4 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
天然气管输服务集中受理分配办结
2022-03-30 3月25日,国家管网集团发布《2022年天然气管道管输服务集中受理工作公告》,标志着首次天然气管输服务集中受理分配工作圆满结束。 此次集中受理采取市场化运作模式分配在役天然 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |