牌号简介 About |
---|
SABIC® HDPE BM6246LS是一种高密度聚乙烯吹塑级高刚性,韧性好,加工性好。这些性能提供了瓶子在较低的重量和非常好的顶部负荷强度。典型应用。SABIC® HDPE BM6246LS通常用于吹塑瓶包装感官敏感产品,例如牛奶、果汁和其他乳制品。不建议用于包装环保材料,如肥皂、清洁剂、洗发水等。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® HDPE BM6246LS is a high density polyethylene blow moulding grade for high rigidity, good toughness and good processability. These properties offer bottles to be made at lower weight with very good top load strength. Typical applications. SABIC® HDPE BM6246LS is typically used for blow moulding bottles for packaging organoleptically sensitive products, e.g. milk, fruit juice and other dairy products. It is not recommended for packaging environmentally active materials such as soaps, detergents, shampoos, etc. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:HDPE HDPE
用途:瓶子;果汁瓶;
加工条件:吹塑成型
性能特点: 机械强度好; 高密度; 韧性好; 易加工; Good Rigidity,Excellent Processability,Good flexibility,High density
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.961 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | |
190℃,21.6kg 190℃,21.6kg |
46 | g/10min | |
190℃,5.0kg 190℃,5.0kg |
2.5 | g/10min | |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%非离子洗涤剂,模压成型,F50 10% non-ionic detergent, molded, F50 |
15.0 | hr | ASTM D1693B |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃,模压成型 -30 ℃, molded |
kJ/m² | ||
23℃,模压成型 23 ℃, molded |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 11357-3 | |
Enthalpy Change Enthalpy Change |
J/g | ISO 11357-3 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吹塑成型料筒温度 Blow molding barrel temperature |
℃ | ||
Blow Molding Melt Temperature Blow Molding Melt Temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 527-2/1BA/50 | |
拉伸强度 tensile strength |
ISO 527-2/1BA/50 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
% | ISO 527-2/1BA/50 | |
弯曲模量 Bending modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中科炼化EVA装置开车成功
2022-03-14 近日,中科炼化10万吨/年EVA装置一次开车成功,填补了中国石化在华南地区EVA生产的空白。 EVA指乙烯-醋酸乙烯共聚物,是国内紧缺的合成材料。与聚乙烯相比,EVA具有更好的柔韧性、 |
中科炼化EVA装置开车成功 近日,中科炼化10万吨/年EVA装置一次开车成功,填补了中国石化在华南地区EVA生产的空白。 EVA指乙烯-醋酸乙烯共聚物,是国内紧缺的合成材料。与聚乙烯相比,EVA具有更好的柔韧性、抗冲击性、填料相溶性和热密封性能,易于加工,附加值高,在发泡、涂覆、电缆、热熔胶等领域应用广泛。近年来,随着国内光伏行业高端化发展,EVA高端产品需求大幅增加,进口依存度维持在较高水平。 中科炼化EVA装置引进釜式法聚合工艺先进技术,是超高压装置,对设备安装、气密等要求很高,开车难度较大。 为保证装置开车成功,中科炼化在总部支持下,与相关单位协商,承担超高压管件国产化制造的重大科技任务,采取国内承建单位制造、国外技术公司监造的方式,于去年12月完成EVA装置全部高压管道的交付安装。 开车前,中科炼化集中力量推进工程建设尾项整改、单机试车、清洗吹扫、联动试车等生产准备工作,稳妥推进查漏消漏工作,最终顺利打通全流程,一次开车成功。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。