Ultramid® B3EG3是一种15%玻璃纤维增强注塑成型PA6级外壳具有增强的抗冲击性。典型应用包括汽车后视镜外壳和山地自行车车轮。 Ultramid B3EG3 is a 15% glass fiber reinforced injection molding PA6 grade for housings with enhanced impact resistance. Applications Typical applications include automotive mirror housings and wheels of moutain bikes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.23 | g/cm³ | ASTM D792 |
密度 Density |
1.23 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,5 kg 275℃,5 kg |
75.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.50 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
7.7 | % | ISO 62 |
饱和 saturated |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ |
kJ/m² | ISO 180 | |
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ||
MD MD |
1/℃ | ASTM E831 | |
MD MD |
1/℃ | ||
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.8 mm 0.8 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
限塑晋级,迎接绿色生活
2018-07-05 塑料污染已成为世界难题。据研究表明,自1950年以来,人类共生产约90亿吨的塑料,截至2015年,就有超过69亿吨成为垃圾。今年世界环境日的主题是“塑战塑决”,旨在呼吁世界各国齐心协力对抗一次性塑料污染问题。 中国在2008年颁布了《国务院办公厅关于限制生产销售使用塑料购物袋的通知》,也就是通常所说的“限塑令”,从源头上减少对塑料袋的使用。“限塑令”成效明显,超市、商场的塑料购物袋使用量普遍减少了2/3以上。 最近,各地继续出台限制塑料使用的新方案,今年,四 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |