牌号简介 About |
---|
陶粒堆肥树脂是可再生的、生态良好的石油基塑料产品替代品,替代了传统塑料中使用的几乎100%的石油基添加剂。陶粒堆肥树脂使用的聚合物和添加剂来自淀粉和其他可再生资源化学。这些成分在最先进的混合设备上小心地混合在一起。所有陶瓷可堆肥树脂,包括可堆肥的4001,在美国和欧洲被认证为可生物降解和可堆肥,符合BPI(可生物降解产品研究所www.bpiworld.com)可堆肥性标准(astm6400d99,astm6868)和欧洲生物塑料标准(en13432)。可堆肥4001的设计具有良好的强度、韧性和加工性平衡。可堆肥4001可在现有的挤压机上加工。有关加工和材料干燥指南,请参阅我们的加工指南。这可以在www.cereplast.com上找到。可堆肥4001推荐用于挤压涂层应用,如杯子、盘子、容器、盒子、纸板等。 Cereplast Compostables® resins are renewable, ecologically sound substitutes for petroleum-based plastic product, replacing nearly 100% of the petroleum-based additives used in traditional plastics. Cereplast Compostables® resins are using polymer and additives derived from starch and other renewable resources chemistry. These components are carefully blended together on state-of-the-art compounding equipments. All Cereplast Compostables® resins, including Compostable 4001, are certified as biodegradable and compostable in the United States and Europe, meeting BPI (Biodegradable Products Institute www.bpiworld.com) standards for compostability (ASTM6400D99, ASTM6868) and European Bioplastics Standards (EN13432). Compostable 4001 has been designed to have an excellent balance of strength, toughness and processability. Compostable 4001 can be processed on existing extrusion machines. Please see our processing guide for processing and material drying guidelines. This can be found at www.cereplast.com. Compostable 4001 is recommended for extrusion coating application like cups, plates, containers, boxes, cardboard and more… |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792-A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2860 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
断裂 fracture |
57.2 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
11 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact |
J | ASTM D5420 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
设计师使石墨烯复合资料的强度和韧性相结合
2017-05-15 就轻质材料的高强度和韧性来说,石墨烯可能算得上王牌。然而,对于最需求这些性能的应用,如航空航天、自动化、基础设施和交通运输,使用石墨烯仍然是太贵和不切实际的。现在,由Markus Buehler领导的麻省理工学院的研究人员通过实验和模拟来设计一种基于氧化石墨烯的复合材料,这种材料针对强度和韧性进行了优化,并展示了湿度如何改善这些性能。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |