| 牌号简介 About |
|---|
| Marlex® HXM 50100是一种高密度 (HMW) 聚乙烯材料,。 该产品在北美洲、拉丁美洲或欧洲有供货,加工方式为:吹塑成型、挤出或热成型。 Marlex® HXM 50100的主要特性有: 阻燃/额定火焰 高分子量 高抗环境应力断裂能力 (ESCR) 己烯共聚单体 坚硬 典型应用领域包括: 汽车行业 容器 罐子 包袋/内衬 工程/工业配件 This extra high molecular weight, ethylene-hexene copolymer is tailored for large blow molded and thermoformed parts that require: Good melt strength Good rigidity Excellent ESCR Excellent low temperature impact strength Durability Recyclability Typical blow molded applications for HXM 50100 include: Shipping containers Jerry cans Fuel containers Agricultural chemical tanks Typical thermoformed applications for HXM 50100 include: Pallets Automotive dunnage Truck bedliners Playground equipment This resin meets these specifications: ASTM D4976 - PE 235 FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per Table 2 of 21 CFR 176.170(c) UL94HB yellow card per UL file E54700 NSF Standard 61 for potable water Listed in the Drug Master File |
产品描述 Product Description
用途：衬里;户外家具;汽车领域的应用;容器;农用水箱;托盘;装运容器;吹制容器;农业应用;油箱;
加工条件：热成型 Thermo forming
性能特点： 防火阻燃等级HB; 熔体强度好; 经久耐用; 耐低温冲击; 己烯共聚单体; 食品接触; 超高分子量; 抗应力开裂; Food contact compliance,Good melt strength,Ultra high molecular weight,Durability,low-temperature impact resistance,Hexene copolymers,High ESCR,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.948 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，21.6kg 190℃，21.6kg |
10 | g/10min | ASTM D1238 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
100%非离子洗涤剂，模压成型，F50 100% non-ionic detergent, molded, F50 |
> 600 | hr | ASTM D1693B |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，模压成型 Shaw's D, molded |
68 | ASTM D2240 | |
|
拉伸强度 tensile strength 2 |
|||
|
屈服，模压成型 Yield, molding 2 |
25.0 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain 2 |
|||
|
断裂，模压成型 Fracture, molded 2 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 3 |
|||
|
正切，模压成型 Tangent, molded 3 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸冲击强度 Tensile impact strength 4 |
|||
|
模压成型 Compression Molding 4 |
kJ/m² | ASTM D1822 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火，模压成型 0.45 MPa, unannealed, molded |
℃ | ASTM D648 | |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746A | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 类型 4, 2.0 in/min |
| 3 0.50 in/min |
| 4 Type S |
| 5 速率 A (50°C/h), 压 力1 (10N) |
|
【新闻资讯】查看全部 
印度：再生塑料允许用于食品接触
2021-11-03 搜料网资讯： 据《印度时报》报道，2021年9月17日，印度修订了他们的塑料废物管理规则，允许在食品接触材料（FCM）中使用再生塑料。根据该修正案，再生塑料 可用于储存、携带、分 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付