| 牌号简介 About |
|---|
| 双峰高密度聚乙烯用于片材挤出和吹塑TIPELIN® 7111S是一种高密度双峰聚乙烯共聚物（以丁烯-1为共聚单体），适用于高刚度、优异的环境应力抗裂性、全缺口蠕变行为和改善长期颜色稳定性的产品的片材挤出和吹塑。该等级包含抗氧化剂和酸清除剂。TIPELIN® 7111S也推荐用于工业零件和消费品包装的片材的挤压，在需要更好的颜色稳定性和更低的产品黄度值的情况下，强烈推荐。TIPELIN® 7111S也推荐用于无压管道挤压和杰瑞罐吹塑，即使是腐蚀性工业化学品的包装。TIPELIN® 7111S适用于食品接触、玩具制造。产品符合食品接触和玩具安全规定。正在接收认证。 Bimodal HDPE for sheet extrusion and blow moulding TIPELIN 7111S is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for sheet extrusion and blow moulding of products with high stiffness, excellent environmental stress crack resistance, full notched creep behavior and improved long-term color stability. The grade contains antioxidants and acid scavengers. TIPELIN 7111S is recommended for the extrusion of sheets of industrial parts and consumer packaging as well, highly recommended in cases when better colour stability and lower yellowness value of the product is needed. TIPELIN 7111S is also recommended for non-pressure pipe extrusion and for blow moulding of jerry cans for the packaging even of aggressive industrial chemicals. TIPELIN 7111S is suitable for food contact, for manufacturing of toys. The product complies with Food Contact and Toy Safety Regulations. Receiving of certifications is in progress. |
产品描述 Product Description
用途：油桶;包装;片材;工业应用;玩具;管道系统;
加工条件：管路挤出成型
性能特点： 可回收; 机械强度好; 抗氧化; 共聚物; 高密度; 颜色稳定; 丁烯共聚单体; 双峰分子量分布; 食品接触; 抗应力开裂; Good Rigidity,Renewable resources,Food contact compliance,Good color stability,Inoxidizability,Copolymer,High density,Butylene copolymer,Bimodal molecular weight distribution,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.949 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
|
190℃，2.16kg 190℃，2.16kg |
0.12 | g/10min | ISO 1133 |
|
190℃，21.6kg 190℃，21.6kg |
13 | g/10min | ISO 1133 |
|
190℃，5.0kg 190℃，5.0kg |
0.50 | g/10min | ISO 1133 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
10%非离子洗涤剂，F50 10% non-ionic detergent, F50 |
> 10000 | hr | ASTM D1693B |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
弯曲模量 Bending modulus |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
µm | ||
|
拉伸强度 tensile strength |
|||
|
断裂，70 µm，吹塑薄膜 Fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
|
屈服，70 µm，吹塑薄膜 Yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，70 µm，吹塑薄膜 Fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
|
屈服，70 µm，吹塑薄膜 Yield, 70 µ m, blow molded film |
% | ISO 527-3 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A120 | |
|
氧感应时间 Oxygen sensing time |
|||
|
200℃ 200℃ |
min | EN 728 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
伊之密2020云开放周受到各方关注
2020-09-21 搜料网资讯： 伊之密2020云开放周9月18日在吴江工厂圆满落幕，现场展出的多个先进成型解决方案及智能制造解决方案受到各方关注。期间，吴江区工信局、区外商投资企业协会、区智 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |