牌号简介 About |
---|
Celanex® 2004-2是一种未填充聚酯,具有良好的流动性和韧性组合。Celanex® 2004-2的典型应用是包含闩锁的电气连接器。Celanex® 2004-2含有一种内部润滑剂。 Celanex 2004-2 is an unfilled polyester that has an excellent combination of flowability and toughness. A typical application for Celanex 2004-2 is electrical connectors containing latches. Celanex 2004-2 contains an internal lubricant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.30 | g/cm³ | ASTM D792, ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,2.16 kg 250℃,2.16 kg |
33.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
1.8 到 2.0 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2400 | MPa | ISO 527-2/1A/1 |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
53.1 | MPa | ASTM D638 |
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/1A/50 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2/1A/50 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ||
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature 1 |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3, ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
-- -- |
ohms·cm | ASTM D257 | |
-- -- |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength 3 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150,IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.00 mm 1.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
3 方法A(短时间) |
【新闻资讯】查看全部 ![]()
苹果数据线有救了?日本研收回全球最坚韧软资料
2017-07-27 北海道大学龚剑萍教授带领的团队研发了一种新材料,它看起来很柔软,但是却和钢铁一样坚韧。事实是,它比碳钢坚硬5倍,同时又兼具了如同橡胶般的弹性。 这种新材料是一种坚硬而可弯曲的网状结构材料。它利用水凝胶(常用于制作隐形眼镜)和玻璃纤维制备得到,也可被认为是纤维增强的新型复合材料。龚剑萍表示,这是迄今为止人类获得的最坚硬软材料。 |
苹果数据线有救了?日本研收回全球最坚韧软资料 北海道大学龚剑萍专家教授领着的精英团队产品研发了一种新材料,它看上去很绵软,可是却和钢材一样坚毅。客观事实是,它比碳素钢硬实5倍,另外又兼顾了好似硫化橡胶一样的延展性。 这类新材料是一种硬实而可弯折的多孔结构材料。它运用水凝胶(常见于制做隐形眼睛)和夹层玻璃纤维制取获得,也可被觉得是纤维增强的新式复合型材料。龚剑萍表明,它是目前为止人们得到的最硬实软材料。 她们的科研成果发布在《先进功能材料》刊物上(journal Advanced Functional Materials)。经科学研究,新式复合型材料展现出远超独立构成部分的强度及其延展性,这说明其坚定性是协同作用的結果。根据较为毁坏材料所需动能,科学研究工作人员们下结论:该纤维增强的水凝胶材料比一般的水凝胶硬实100倍,比一般的夹层玻璃纤维材料硬实25倍。 图 |新式纤维增强水凝胶 龚剑萍表明,制取该材料的设计灵感来自于自然界。她讲,“每每我看到一朵花从十分硬实的路面(例如建筑裂缝)长出去时,我也觉得十分好奇心,为什么这般小而讨人喜欢的花瓣会出现这么大的动能可以破‘硬地’而出。实际上,疑胶就如同花朵一样,看上去十分绵软、柔弱,可是它是能够 造就极大动能。” 因为其可信性、持续性及其柔韧度,纤维增强的水凝胶具有许多潜在性运用,例如时尚潮流和生产制造主要用途、作为微生物材料(生产制造承担强负载支撑力的人造肌腱和筋腱)。除此之外,它还能够作为人造骨节,并比真实的骨节要硬实。现有好几个企业与龚剑萍精英团队探讨了在开发设计人造软骨组织层面的项目合作。 龚剑萍表明,该纤维增强的水凝胶水分含量40%,并且十分环境保护,除开用以生产制造人造机构,还能够运用在运动装和防护衣行业,例如作帽子和防弹背心。 自然,这一結果并并不是最极致的,但一样对相近的科学研究拥有 开拓性实际意义。 来源于:DeepTech深科技 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。