| 牌号简介 About |
|---|
| CALIBRE™ 300-6 聚碳酸酯树脂具有吹塑模塑和片材应用领域所需的优异的抗冲击性能、耐热畸变性能和光学透明度以及高熔体强度。CALIBRE 300-6系列产品包含有4种添加剂产品类型： CALIBRE 300：无脱模剂或者抗紫外线稳定剂。CALIBRE 301：含脱模剂。 CALIBRE 302：含抗紫外线稳定剂。CALIBRE 303：含脱模剂和抗紫外线稳定剂。 政府和业界标准： 加拿大标准协会(CSA)的要求 美国安全检测实验室 (UL)的要求 应用领域： 汽车内饰 汽车外饰 片材应用 照明/开关 小型与大型电器 饮料容器/服务用品 电力设备 CALIBRE™ 300-6 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, and optical clarity as well as high melt strength for blow molding and sheet applications. The CALIBRE 300-6 series products are available in 4 additive packages: CALIBRE 300: No mold release or UV Stabilizer. CALIBRE 301: Mold release. CALIBRE 302: UV stabilizer. CALIBRE 303: Mold release and UV stabilizer. Govt. and Industry Standards: CSA (Canadian Standards Association) Underwriters Laboratory, Inc. (UL) Applications: Automotive interiors Automotive exteriors Sheet applications Electrical lighting/switches Small & large appliances Beverage containers/serviceware Power equipment |
产品描述 Product Description
用途：电气/电子应用领域;汽车领域的应用;照明应用;片材;容器;汽车外部零件;电器用具;汽车内部零件;
加工条件：片材挤出成型
性能特点： 防火阻燃等级HB; 熔体强度好; 透光性好; 冲击性能好; Good Clarity,High impact resistance,Good melt strength,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
密度 Density |
1.20 | g/cm³ | ISO 1183/A |
|
密度 Density |
1.2 | g/cm³ | ISO 1183-2 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
6.0 | g/10min | ASTM D1238 |
|
300℃，1.20kg 300℃，1.20kg |
6.0 | g/10min | ISO 1133 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
cm³/10min | ISO 1133 | |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
% | ISO 294-4 | |
|
MD MD |
% | ASTM D955 | |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
23℃，24hr 23℃，24hr |
% | ISO 62 | |
|
23℃，24hr 23℃，24hr |
% | ASTM D570 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA 2 | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA 2 | |
|
简支梁冲击强度 Charpy impact strength |
|||
|
23℃ 23℃ |
ISO 179/1eU 2 | ||
|
-30℃ -30℃ |
ISO 179/1eU 2 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180-A | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
ASTM D256 | ||
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
ISO 180 | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 6 |
|||
|
23℃，Total Energy 23℃，Total Energy 6 |
J | ASTM D3763 | |
|
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa 1.8 MPa |
℃ | ISO 75-2 2 | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
|
0.45 MPa 0.45 MPa |
℃ | ISO 75-2 2 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 7 | |
|
B50 B50 |
℃ | ISO 306 | |
|
B50 B50 |
℃ | ISO 306 2 | |
|
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-40~82℃ MD：-40~82℃ |
1/℃ | ASTM D696 | |
|
MD MD |
1/℃ | ISO 11359-2 2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 2 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 2 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相对电容率 Relative permittivity |
|||
|
100 Hz 100 Hz |
IEC 60250 2 | ||
|
1 MHz 1 MHz |
IEC 60250 2 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
100 Hz 100 Hz |
IEC 60250 2 | ||
|
1 MHz 1 MHz |
IEC 60250 2 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
|||
|
2.00 mm，解决方案 A 2.00 mm, solution A |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level 8 |
UL 94 | ||
|
1.60 mm 1.60 mm |
UL 94 | ||
|
3.20 mm 3.20 mm |
UL 94 | ||
|
阻燃等级 Flame retardant level |
|||
|
3.20 mm 3.20 mm |
ISO 1210 2 | ||
|
极限氧指数 Extreme oxygen index 8 |
% | ISO 4589-2 | |
|
氧指数 Oxygen index |
% | ISO 4589-2 2 | |
|
平均燃烧程度 Average combustion degree |
cm | ASTM D635 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index |
ASTM D542 | ||
|
折射率 Refractive index |
ISO 489 | ||
|
透光率 Transmittance |
% | ASTM D1003 | |
|
雾度 Haze |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 3 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
屈服 yield |
MPa | ISO 527-2 2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture 4 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
屈服 yield |
% | ISO 527-2 2 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
Nominal strain at break Nominal strain at break |
% | ISO 527-2 2 | |
|
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 |
MPa | ISO 178 | |
|
泰伯耐磨性 Taber abraser |
% | ASTM D1044 | |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
|
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.60 mm 1.60 mm |
ISO 1210 2 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 2,0 in/min |
| 4 方法 I (三点负荷), 0,079 in/min |
| 5 0,079 in/min |
| 6 11,1 ft/sec |
| 7 速率 A (50°C/h), 载荷2 (50N) |
| 8 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
| 9 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
|
【新闻资讯】查看全部 
2018中国新资料产业开展大会暨展览会
2018-10-25 为深入贯彻落实党的十九大精神，对标新时代，紧扣新要求，助力推进我国新材料产业健康快速发展，由中国材料研究学会发起，联合国家新材料产业发展专家咨询委员会共同主办系列“2018中国新材料产业发展大会暨展览会”。大会旨在服务国家新材料发展战略，服务新材料特色产业，服务新材料创新创业。 本次大会形式包括大会报告、分论坛研讨、圆桌会议和产学研对接，大会成果将以新材料发展蓝皮书和产业发展报告的形式向社会公开发布。 大会同 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付