牌号简介 About |
---|
拉努芬LLF181H是一种线性低密度通用吹塑薄膜挤出聚乙烯,具有较高的机械性能和良好的加工性能。拉努芬LLF 181H含有防滑添加剂和防堵剂。由该树脂制备的薄膜具有良好的韧性、高拉伸性能、优异的耐穿刺性和良好的光学性能。拉努芬LLF 181H被推荐用于一般用途的吹塑薄膜的制造,如工业衬垫、食品包装和农业薄膜。 LANUFENE LLF 181H is a linear low density polyethylene for general purpose blown film extrusion with high mechanical properties and good process-ability. LANUFENE LLF 181H contains slip additive and anti-blocking agent. The film produced from this resin characteristically exhibits good toughness, high tensile properties, outstanding puncture resistance and good optical properties. LANUFENE LLF 181H is recommended for the manufacture of general purpose blown films such as industrial liners, food packaging and agricultural film. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:38 µm 1% secant, MD: 38 µ m |
220 | MPa | ASTM D882 |
1% 正割,TD:38 µm 1% secant, TD: 38 µ m |
260 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
极限 limit |
MPa | ASTM D638 | |
MD,断裂,38 µm MD, fracture, 38 µ m |
MPa | ASTM D882 | |
TD,断裂,38 µm TD, fracture, 38 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture |
% | ASTM D638 | |
MD,断裂,38 µm MD, fracture, 38 µ m |
% | ASTM D882 | |
TD,断裂,38 µm TD, fracture, 38 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm 38 µm |
g | ASTM D1709-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,38 µm 45°,38 µm |
ASTM D2457 | ||
雾度 Haze |
|||
38 µm 38 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
GET!!注塑或塑料加工检验术语及定义!请收藏~
2016-07-19 塑料件注塑加工检验技术术语 熔接痕(俗称:夹水纹;其它名称:夹线、夹纹) 定义:在注塑加工过程中,两股料流相遇时,其世界面处未完全熔合而造成的痕迹。 缩痕(俗称:缩水;其它名称:无) 定义:塑料件在模腔内冷却凝固时,由于塑料件壁厚不均匀、射胶压力不足、冷却时间不够等原因而在塑料件表面产生的凹陷。 技术术语:无(俗称:气纹;其它名称:无) |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |