牌号简介 About |
---|
Bayflex® 953是一种全复合聚醚型聚氨酯系统,由两种液体成分组成,可以喷水。A组分为改性二苯基甲烷二异氰酸酯(MDI)预聚物,B组分为聚醚多元醇体系。Bayflex® 953系统用于制造微孔聚氨酯鞋底。由这些部件制成的鞋底结合了重量轻、舒适和耐用性。在各种密度下,加工性能和动态弯曲性能都很好。优良的物理性能和易于加工的结合使Bayflex® 953系统成为时尚和休闲鞋单密度鞋底的主要材料。与任何产品一样,用户必须提前对给定应用中Bayflex® 953系统的使用进行测试(包括但不限于现场测试),以确定其适用性。 Bayflex 953 is a fully compounded polyether-based polyurethane system consisting of two liquid components which can be water-blown. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. The Bayflex 953 system is used in the manufacture of microcellular polyurethane shoe soles. Soles prepared from these components combine light weight, comfort, and durability. Processibility and dynamic flexural properties are excellent over a wide range of densities. The combination of excellent physical properties and ease of processing has made the Bayflex 953 system a prime material for single-density soles for fashion and casual shoes. As with any product, use of the Bayflex 953 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.520 | g/cm³ | 内部方法 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
3.10 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
400 | % | ASTM D412 |
撕裂强度 tear strength |
|||
-- -- 2 |
4.38 | kN/m | 内部方法 |
-- -- 3 |
14.0 | kN/m | ASTM D1004 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components 4 |
|||
部件 A Component A |
|||
部件 B Component B |
|||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐油性 Oil resistance |
|||
Volume Swell Volume Swell |
% | ASTM D5694 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D3489 | |
Ross曲折测试 - 0% Cut Growth Ross Twist Test -0% Cut Growth |
ASTM D1052 | ||
-29℃,6.35 mm -29℃,6.35 mm |
Cycles | ASTM D1052 | |
23℃,6.35 mm 23℃,6.35 mm |
Cycles | ASTM D1052 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Block |
3 C 模具 |
4 98 Index |
【新闻资讯】查看全部
上海市石油学会助力第十届中国石化聚焦峰会顺利召开!
2016-03-10 近日,中国七大炼化基地的首个省级规划浮出水面。江苏省“敢为天下先”,首先提出要为全国石化产业转型升级作示范,其公布了《石化产业规划布局方案》“江苏版”,并提出将“调整存量、提升增量、优化总量、突出特色”作为导向,并对连云港石化基地做出了中长期发展规模的方案。 2014年6月份的国务院常务会议上,李克强总理曾定调石化产业发展原则,提出要打造世界一流的产业基地,其中入选的七大石化产业基地包括:大连长兴岛(西中岛)、上海漕泾、广东惠州、福建古雷、河北曹妃甸、江苏连云港以及浙江宁波 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |