牌号简介 About |
---|
500S系列是非常有利的透明度和良好的耐刮性要求,以及有较高的表面光洁度要求。未填充级具有良好的流动和机械性能,如延伸率、压缩永久变形、拉伸和撕裂强度。与600S和660S系列相比,低密度需要更低的重量。未填充化合物的硬度范围为0肖氏A至55肖氏D,呈半透明和黑色,但在任何阴影下都可以轻易着色。 The 500S series is very favourable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mechanical properties, such as elongation, compression set, tensile and tear strength. The low density entails lower weight compared to the 600S and 660S series. Unfilled compounds are available in hardness from 0 Shore A to 55 Shore D in translucent and black colours but they can easily be coloured in any shade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.890 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
0.80 to 2.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
60 | ASTM D2240 | |
拉伸强度 tensile strength |
ASTM D638 | ||
-- -- |
7.00 | MPa | ASTM D638 |
100% 应变 100% strain |
MPa | ASTM D638 | |
300% 应变 300% strain |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
|||
23℃,72 hr 23℃,72 hr |
% | ASTM D395 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
使用温度 Operating temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
我国塑机工业经济目的继续回升
2016-12-30 据中国塑料机械工业协会数据,2016年1~10月,我国塑料机械制造规模以上企业402家,主营业务收入和利润总额自3月起回升,第三季度同比增长24%;10月份主营业务收入、利润总额和出口交货值分别同比增长19%、59%和11%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |