牌号简介 About |
---|
TPX® DX560M是一种聚甲基戊烯共聚物(PMP 共聚物)材料,。 该产品在北美洲有供货,加工方式为:吹塑成型、管路挤出成型、挤出、型材挤出成型或注射成型。 TPX™ DX560M TPX™ DX560M is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for blow molding, extrusion, injection molding, pipe extrusion, or profile extrusion. TPX™ DX560M TPX™ is a 4-methylpentene-1-based olefin copolymer. TPX™ has a unique molecular structure. Although TPX™ is a crystalline olefin polymer, it shows transparency. Because of its excellent heat-resistance, release property and chemical resistance, TPX™ is used for industrial materials, including mandrels and sheaths in the manufacture of high-pressure rubber hose, mold cups to create LED light and other applications such as release film on FPC manufacturing process and release paper in the manufacture of synthetic leather. Furthermore, TPX™ possesses a lowest density among thermoplastic polymers and then provides the molded articles with lower weight. This leads to reduce the environmental load for transportation. It is also noted that TPX™ is a halogen-free polymer denoted as environmentally-friendly material. TPX™ is also used for food-related applications such as food wraps, food preservation packs, baking carton and microwave oven tableware. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.856 | g/cm³ | 内部方法 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,5.0kg 260℃,5.0kg |
33 | g/10min | 内部方法 |
吸水率 Water absorption rate |
|||
饱和 saturated |
< 0.010 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
注塑 Injection molding |
500 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃,注塑成型 23 ℃, injection molding |
无断裂 | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 4 |
|||
0.45 MPa,未退火,6.35 mm 0.45 MPa, unannealed, 6.35 mm 4 |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-10~160℃ MD:-10~160℃ |
1/℃ | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity 6 |
|||
2 mm 2 mm 6 |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 6 |
|||
2 mm 2 mm 6 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant 6 |
|||
2.00 mm,1 MHz 2.00 mm,1 MHz 6 |
ASTM D150 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus 2 |
|||
23℃,注塑成型 23 ℃, injection molding 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 2 |
ASTM D638 | ||
屈服,23℃,注塑成型 Yield, 23 ℃, injection molding |
MPa | ASTM D638 | |
断裂,23℃,注塑成型 Fracture, 23 ℃, injection molding |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂,23℃,注塑成型 Fracture, 23 ℃, injection molding 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
3.20 mm,注塑成型,51 mm跨距 3.20 mm, injection molded, 51 mm span 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
|||
3.20 mm,注塑成型,51 mm跨度 3.20 mm, injection molded, 51 mm span 3 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 4, 2.0 in/min |
3 0.051 in/min |
4 120°C/hr |
5 速率 A (50°C/h), 压 力1 (10N) |
6 Injection Molded |
【新闻资讯】查看全部
2017年中国医药胶塞领域耗费原资料约5万吨
2018-05-10 2018年4月26日,国家药品监督管理局发布通告称,“为指导药品与包装容器系统的相容性研究工作,建立并完善药品与包装相容性研究指导原则体系,组织制定了《化学药品与弹性体密封件相容性研究技术指导原则(试行)》”。 据不完全统计,2017年中国医药胶塞领域消耗原材料约5万吨,年增长率不到5%。相反,热塑性弹性体材料(TPE)在该领域的消耗年增长率则高达15%。针对目前中国医药包装市场依旧参差不齐的原料情况,此次发布的指导原则更是展现出各类医药包装领域新材料的蓬勃发展。而这长达4 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |