| 牌号简介 About |
|---|
| 低密度湿固化聚乙烯化合物，用于低压建筑电线、控制电缆和电缆槽应用（UL型SIS、XHH、XHW、XHW-2、RHH、RHW和RHW-2 VW-1）。Pexidan® V/T-2是一种低密度交联聚乙烯系统，可通过水分固化，由硅烷预接枝的碱化合物A-3001和催化剂母粒CAT-045FR（Sioplas方法）组成。混合和挤压成适当的比例（50/50），这两种成分导致一种材料，可通过暴露在热水中固化。pexidan v/t是符合RoHS的系统。 Low Density Moisture Curable Polyethylene Compound For Low Voltage Building Wire, Control Cable and Cable Tray Applications (UL Styles SIS, XHH, XHHW, XHHW-2, RHH, RHW, and RHW-2 VW-1) 1 . Also CSA listed for RW-90 and CIC (-40C rated) PEXIDAN ® V/T-2 is a low density flame-retardant XLPE system curable by moisture and consists of a silane-grafted base compound A-3001 and a catalyst masterbatch CAT-045FR. Mixed and extruded in the proper proportions (50/50), the two components result in a material that is curable by exposure to hot water. PEXIDAN ® V/T-2 is halogenated but is RoHS-compliant. |
产品描述 Product Description
用途：电线电缆应用;低压绝缘;
加工条件：挤出 Extrusion
性能特点： 可交联; 低密度; Crosslinked,Low density
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.32 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
交叉结合的程度 The degree of cross combination |
60 | % | ASTM D2765 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
15.2 | MPa | UL 1581 |
|
断裂 fracture 2 |
16.5 | MPa | UL 1581 |
|
断裂 fracture 3 |
MPa | UL 1581 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | UL 1581 | |
|
断裂 fracture 3 |
% | UL 1581 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
变形 deformation |
% | UL 1581 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
相对电容率 Relative permittivity |
|||
|
90℃ 90℃ |
UL 1581 | ||
|
击穿电压 breakdown voltage |
UL 1581 | ||
|
-- -- |
V | UL 1581 | |
|
after glancing impact after glancing impact |
V | UL 1581 | |
|
绝缘电阻 insulation resistance |
UL 1581 | ||
|
15℃ 15℃ |
Mohms/1000 ft | UL 1581 | |
|
90℃ 90℃ |
Mohms/1000 ft | UL 1581 | |
|
after 12 weeks：90℃ after 12 weeks：90℃ |
Mohms/1000 ft | UL 1581 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
极限氧指数 Extreme oxygen index |
|||
|
4.0 mm 4.0 mm |
% | ASTM D2863 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Crushing Test Crushing Test |
g | UL 1581 | |
|
高温伸长率 High temperature elongation 4 |
|||
|
负荷下伸长率，150℃ Elongation under load, 150 ℃ 4 |
% | 内部方法 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 After 60 day oil @ 75°C |
| 3 After 30 day gasoline @ 23°C |
| 4 After thermal ageing (7days @121°C) |
| 5 15 minutes, 0.2 N/mm² load |
|
【新闻资讯】查看全部 
11月塑料制品产量增速上升 同比下跌2.5%
2016-12-26 据前瞻数据库数据显示，2016年11月我国塑料制品产量704.7万吨，同比上涨2.5%。 以下为2016年1-11月我国塑料制品产量统计： 相对于金属、石材、木材，塑料制品具有成本低、可塑 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付