牌号简介 About |
---|
优异的抗应力、抗裂性和刚度、高冲击强度、中等膨胀、高熔体强度符合:美国FDA 21 CFR 177.1520(c)3.2A美国FDA-DMF加拿大HPFB无异议(有限制),欧盟10/2011号保险商实验室公司(ULI),详细信息请参考相关法规。UNIVAL™ DMDA-6200 NT 7高密度聚乙烯(HDPE)树脂是一种多用途聚合物,设计用于高速生产吹塑容器,用于包装家用工业化学品(如洗涤剂、漂白剂、织物柔软剂)、洗漱用品和化妆品(如洗发水、面霜、洗剂等)、保健和医疗辅助用品以及食品。此外,它可以吹塑成其他薄壁零件和家居用品,也可以挤压成型材。 Excellent stress crack resistance and rigidity High impact strength Moderate swell High melt strength Complies with: U.S. FDA 21 CFR 177.1520 (c) 3.2a U.S. FDA-DMF Canadian HPFB No Objection (with Limitations) EU, No 10/2011 Underwriters Laboratories Inc. (ULI) Consult the regulations for complete details. UNIVAL™ DMDA-6200 NT 7 High Density Polyethylene (HDPE) Resin is a multipurpose polymer designed for high speed production of blow molded containers used to package household industrial chemicals (e.g., detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.), health and medicinal aids, and food products. In addition, it can be blow molded into other thin walled parts and houseware items, and also can be extruded into profiles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.953 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.38 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
33 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,100%非离子表面活性剂,F50 50 ℃, 100% non-ionic surfactant, F50 |
80.0 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength 4 |
168 | kJ/m² | ASTM D1822 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服 yield |
% | ASTM D638 | |
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
2% 正割 2% secant |
MPa | ASTM D790-B |
备注 |
---|
1 With limitations |
2 一般属性:这些不能被视为规格。 |
3 类型 S |
【新闻资讯】查看全部
中国关于美国循环经济和回收行业起着重要作用
2018-09-25 在很长一段时间,塑料的生产、流通和再生都不是在单一国家完成整个生命周期的变化。因为中国是全世界的制造中心,需要大量的塑料原料,所以在2016年以前,中国承担着全世界废旧塑料处理和贸易的中转基地和最终目的地的角色。 而中国的“禁废令”实施以来,全球塑料贸易链被重置,大多数发达国家受此影响,特别是美国,在2017年以前,美国有50%的废塑料会运到中国,所以说中国对于美国循环经济和回收行业起着重要作用。 在9月13-14日召开的ChinaReplas2018中国塑 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |