| 牌号简介 About |
|---|
| Kraton D1114 P是一种透明的线性三嵌段共聚物，以苯乙烯和异戊二烯为基础，聚苯乙烯含量为19%。它是从北美供应的，物理形式如下所示。Kraton D1114 PT-作为粉末状致密颗粒提供，Kraton D1114 PSM-作为粉末提供，粉末上撒有硅石Kraton D1114 P，用作配制粘合剂、密封剂和涂层的成分。它也可以用作沥青或热塑性塑料的改性剂和化合物配方。 Kraton D1114 P is a clear, linear triblock copolymer based on styrene and isoprene with a polystyrene content of 19%. It is supplied from North America in the physical form identified below. Kraton D1114 PT - supplied as a dusted dense pellet Kraton D1114 PSM - supplied as a powder dusted with silica Kraton D1114 P is used as an ingredient in formulating adhesives, sealants and coatings. It may also find use as a modifier of bitumen or thermoplastics and in compound formulations. |
产品描述 Product Description
用途：塑料改性;粘合剂;密封剂;复合;涂层应用;
颜色：清晰/透明
加工条件：压缩模塑
性能特点： 抗氧化; 共聚物; Inoxidizability,Copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.920 | g/cm³ | ASTM D4025 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
200℃，5.0kg 200℃，5.0kg |
7.0 到 13 | g/10min | ASTM D1238 |
|
Antioxidant Additive Antioxidant Additive 2 |
0.080 到 0.30 | % | 内部方法 |
|
聚苯乙烯含量 Polystyrene content |
17 到 21 | % | 内部方法 |
|
Total Extractables Total Extractables |
< 1.0 | % | 内部方法 |
|
灰份含量 Ash Content |
|||
|
PSM PSM 3 |
% | ISO 247 | |
|
滑石 talc |
% | 内部方法 | |
|
挥发物 Volatiles |
% | 内部方法 | |
|
溶液粘度 Solution viscosity |
|||
|
25wt%甲苯，25℃ 25wt% toluene, 25 ℃ |
mPa·s | 内部方法 | |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ASTM D412 | |
|
300% 应变 300% strain |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D412 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Diblock Content Diblock Content |
|||
|
Styrene/Rubber ratio Styrene/Rubber ratio |
|||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Primary antioxidant is a non-staining, phenolic antioxidant. The antioxidant package also contains a non-TNPP secondary antioxidant at a target level of 0.2% wt. |
| 3 The final dusting level is a combination of the talc from the original D1114 PT and silica added during the milling process. |
|
【新闻资讯】查看全部 
年产40万吨己内酰胺聚酰胺6芯片集成项目落户新疆奇台县
2022-07-05 6月29日，新疆奇台县人民政府与新疆宏顺新材料有限公司在昌吉市签署项目投资协议，在奇台县建设40万吨/年己内酰胺-聚酰胺6切片集成项目。 据搜料网了解，该项目总投资76亿元，主 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付