牌号简介 About |
---|
一种生物相容性改性聚苯醚,具有医疗保健应用的标准流程。 Biocompatible, modified Polyphenylene Ether with standard flow for healthcare applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,5.0kg 300℃,5.0kg |
8.4 | g/10min | ASTM D1238 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.050 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
57.2 | MPa | ASTM D638 |
屈服 yield |
70.3 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
运用最佳拟合法拟合坐标系的办法
2015-12-10 数模坐标系与零件坐标系拟合在一起,是我们使用最佳拟合法中最常使用的方法之一。这种方法适用于可以构造或测量的零件,评价方法要是在原始数模坐标系下或数模坐标系比较复杂的情况下,直接用3-2-1法拟合难度会很大。下面就让思瑞测量为您介绍一种最佳的拟合坐标系的方法。 最佳拟合法拟合坐标系的步骤如下: 1.导入数模后,在数模上用程序模式测量、构造至少3个方向都与零件相关的点(这些点可以是:圆柱与平面的刺穿点、加样点测量的圆心点、两个空间圆柱轴线的交点、三个平面的相交的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |