牌号简介 About |
---|
MARCOBLEND 6000 H BK是一种阻燃聚碳酸酯/ABS树脂,该树脂无卤,符合TCO和RoHS认证。其独特的特点是加工性能优越,光泽等级高,刚度好,尺寸稳定性好,适用于TFT液晶显示器框架和内部结构件。 MARCOBLEND 6000 H BK is an ignition resistant polycarbonate/ABS resin.The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, High gloss grade good stiffness, and excellent dimension stability and suitable for use in TFT LCD frame and internal structure parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.30-0.50 | % | ASTM D995 |
熔体质量流动速率 Melt Flow Rate |
|||
240℃,5.0kg 240℃,5.0kg |
30 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
66.40 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
50 | % | ASTM D638 |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
|
V-0 | UL 94 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
桑托斯和SK在澳大利亚开展CCS项目
2022-03-06 据世界天然气2月28日消息称,澳大利亚能源巨头桑托斯已与韩国绿色能源公司 SK ES 合作开展碳捕获和储存项目。 Santos、SK ES、K-CCUS协会、CO₂CRC和韩国贸易保险公司签署了一份谅解备忘 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |