牌号简介 About |
---|
Adstif HA612M是一种高结晶度聚丙烯均聚物,具有极高的刚度、良好的透明度和优异的高温性能。它特别适用于要求高刚性、高透明度和良好热特性的铸膜应用。Adstif HA612M特别推荐用于高速包装线上缠绕包装用Coex薄膜的生产。其他应用包括花卉和纺织品包装,可消毒和巴氏灭菌食品包装。Adstif HA612M既不含滑动剂,也不含防阻塞剂,适用于金属化薄膜。它不含硬脂酸钙。有关监管信息,请参阅Adstif HA612M产品管理公告(PSB)。 Adstif HA612M is a high crystallinity polypropylene homopolymer with an extremely high stiffness, good transparency and outstanding high temperature performances. It is especially designed for cast film applications where high rigidity, transparency and very good thermal characteristics are required. Adstif HA612M is particularly recommended for the production of coex film for Twist Wrapping on high speed packaging lines. Other applications include flowers and textile packaging, sterilizable and pasteurizable food packaging. Adstif HA612M does not contain neither slip nor antiblocking agents and is suitable for metallisable films. It is Calcium Stearate free. For regulatory information please refer to Adstif HA612M Product Stewardship Bulletin (PSB). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
7.0 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
割线模量 Secant modulus 2 |
|||
MD,50 µm,铸造薄膜 MD, 50 µ m, cast thin film 2 |
900 | MPa | ASTM D882 |
拉伸强度 tensile strength 3 |
ASTM D882 | ||
MD,屈服,50 µm,挤塑薄膜 MD, yield, 50 µ m, extruded film |
22.0 | MPa | ASTM D882 |
MD,断裂,50 µm,挤塑薄膜 MD, fracture, 50 µ m, extruded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
MD,屈服,50 µm,挤塑薄膜 MD, yield, 50 µ m, extruded film |
% | ASTM D882 | |
MD,断裂,挤塑薄膜 MD, fracture, extruded film |
% | ASTM D882 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,铸造薄膜 45 °, 50.0 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,铸造薄膜 50 µ m, cast thin film |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
屈服 yield |
% | ISO 527-2 | |
断裂 fracture |
% | ISO 527-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,98 in/min |
3 20 in/min |
【新闻资讯】查看全部
聚氨酯彩钢板在建筑保温防水范畴的使用分析
2016-03-16 聚氨酯原料在各行业应用非常广泛,因应用的行业特性和生产的产品不同,各行业对以聚氨酯为主要原料的组合材料的性能要求也不同。承担保温防水双功能的聚氨酯硬泡 (SPF)也完全不同于用于冰箱、冷库仅起保温作用的聚氨酯(PUR),尽管它们外观结构看似非常相像,但作为建筑保温防水一体化材料,聚氨酯硬泡打破了传统建材功能单一、防水的不保温、保温的不防水、防水层一旦出现渗漏、保温层随即失去保温功能的通病。与其它单功能保温或防水材料相比,聚氨酯硬泡具有明显的优势: 聚氨酯彩钢板1、聚氨酯硬泡 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |