牌号简介 About |
---|
CELEX 720GS 是一种20%玻璃纤维增强的聚碳酸酯树脂。它具有刚性高和尺寸稳定好的特点。CELEX 720GS用于制作计算机的冷却风扇、传真机机壳、显示器底座和空调机零部件。 CELEX 720GS is a 20% glass fiber reinforced ABS resin. It is designed with high rigidity and good dimensional stability. CELEX 720GS is designed for use in computer cooling fan, fax machine chassis, monitor base and air-conditioner parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 | % | ASTM D995 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
2.5 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
74.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
|||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
4220 | MPa | ASTM D638 |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.00mm 1.00mm |
UL-94 | ||
2.40mm 2.40mm |
UL-94 | ||
2.60mm 2.60mm |
UL-94 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
4千到8万,动力电池回收生意太抢手!原料涨价引爆整个产业
2022-03-21 近一年来,新能源汽车产销量持续创下新高,原材料供需矛盾日益突出,涨价压力下,变废为宝的动力电池回收行业价值链获得重估,景气度开始攀升,引来产业资本竞相入局。 在原材 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |