牌号简介 About |
---|
通用聚苯乙烯,流动性好,耐热性高。N 3782属于Edistir GPPS第三代。第三代Versalis GPP以其色彩更加明亮和中性而著称,符合更复杂的市场需求。建议用于大规格绝缘板(XPS)的直接充气挤出,并与高浓度透明SBS混合,以提高板材的透明度和刚度。名称:热塑性塑料ISO 1622-PS,E,105-06。适用于绝缘板(XPS)、透明板和热成型透明包装。 General purpose polystyrene with good flow and high heat resistance. N 3782 belongs to Edistir® GPPS third generation. The third generation of versalis GPPS distinguished for a colour more brilliant and neutral in line with more sophisticated market needs. Suggested for direct gassing extrusion of heavy gauge insulating boards (XPS) and in blend with high concentration of clear SBS for improving clarity and stiffness of the sheets. Designation: Thermoplastics ISO 1622-PS,E,105-06. Applications Designed for insulation panels (XPS), clear sheets and thermoformed clear packaging. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.65 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
7.5 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.30 到 0.60 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.10 | % | ISO 62 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
12℃ 12℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 3 |
|||
1.8 MPa,退火 1.8 MPa, annealed 3 |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
50 Hz 50 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
50 Hz 50 Hz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.50 mm,所有颜色 1.50 mm, all colors |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Designation Designation |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ISO 2039-2 | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/5 | |
弯曲强度 bending strength 2 |
MPa | ISO 178 |
备注 |
---|
2 2.0 mm/min |
3 120°C/hr |
【新闻资讯】查看全部
李在镕假释出狱,对三星“帝国”意味着什么?
2021-08-16 搜料网资讯: 8月13日上午10时,三星集团实际控制人,三星电子副会长李在镕获假释出狱。时隔207天,李在镕重获自由身。 法务部长官朴范界表示,综合考虑新冠疫情常态下国内外经济 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |