| 牌号简介 About |
|---|
| Kynar-Flex 2800-00是一种基于VF 2的颗粒状半结晶共聚物。Kynar flex 2800-00专门设计用于电线和电缆结构以及其他需要高灵活性和提高抗冲击性的用途。对于化学应用，它可以挤压成片材和管子。Kynar Flex 2800-00可以注塑成型。优点：在零下温度-20°C（-4°F）下提高了灵活性，在-20°C（-4°F）下提高了抗应力开裂能力，提高了断裂延伸率。附加特点：易于加工，使用常规设备，具有优异的热稳定性，老化后具有优异的耐化学性，符合UL 910烟雾和火焰R。电缆护套等要求UL温度额定值125°C辐射交联 Kynar Flex® resins are fluorinated thermoplastic copolymers. Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties. Main applications: flexible tubing, corrosion protection in the chemical industry, coating (painting, co-extrusion), off shore, wire and cable jacketing with and without cross-linking. Kynar Flex® 2800-00 resin is a standard grade of granules, compared to the homopolymer grades, which exhibits a lower modulus, a better resistance to stress cracking in alkaline and oxidizing media, and a lower melting point. For cable coating, extrusion of tube and plaque, compression molding of bulky parts. Additional characteristics: Easily processed using conventional equipment Excellent thermal stability Retains properties after aging Pigmentable UL RTI temperature rating 125°C Radiation crosslinking |
产品描述 Product Description
用途：片材;电线电缆应用;管件;
加工条件：注射成型 Injection Molding
性能特点： 耐低温柔性; 热稳定性好; 耐化学性; 冲击性能好; 抗应力开裂; 韧性好; 易加工; Excellent Processability,Good flexibility,High impact resistance,Low temperature toughness,Solvent resistance,Heat Stabilized,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
熔融峰值温度 Melting peak temperature |
140 到 145 | ℃ | ASTM D3418 |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity 3 |
|||
|
20 ℃ 20 ℃ 3 |
2.0E+14 | ohms·cm | ASTM D257 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，23℃ Shore D, 23 ℃ |
60 到 70 | ASTM D2240 | |
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
屈服，23℃ Yield, 23 ℃ |
20.0 到 34.5 | MPa | ASTM D638 |
|
断裂，23℃ Fracture, 23 ℃ |
17.2 到 34.5 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
|||
|
23℃ 23℃ |
MPa | ASTM D695 | |
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ASTM D792 | |
|
熔体表观粘度 Apparent viscosity of melt |
|||
|
232℃，100 sec^-1 232℃，100 sec^-1 |
Pa·s | ASTM D3835 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 65% R.H. |
|
【新闻资讯】查看全部
赢创扩产ROHACELL品牌功用性泡沫
2016-11-23 赢创拟扩大德国达姆施塔特工厂功能性泡沫生产产能。投资扩建以后，该工厂约能提高20%的产量。 该公司还将增加新的生产设备，生产产品将以ROHACELL品牌推出市场。产能扩大部分预计将于明年开始市场流通。 赢创功能性聚合物业务高级副总裁Matthias Kottenhahn说：ROHACELL这一品牌已经连续几年维持在两位数的增长，按照现阶段情况，还有望延续这一上升趋势。随着全球需求的增长，我们认为扩建是正确且必要的一步，以保证客户现在和以后都能使用到我们的最新 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |