牌号简介 About |
---|
Styrolux® BX6400是一种开发性的高清晰度和极限韧性的苯乙烯-丁二烯共聚物(SBC),主要用于片材和薄膜挤出和热成型应用。它是专门为提高与通用聚苯乙烯的混合性能而设计的,为零件提供了良好的韧性和透明度平衡。特点突出的韧性高GPPS混合能力出色的清晰度应用食品包装食品服务项目饮用杯挤压薄膜 Styrolux® BX6400 is a developmental styrene butadiene copolymer (SBC) of high clarity and ultimate toughness used mainly in sheet and film extrusion and thermoforming applications. It is specifically designed for improved performance in blends with general-purpose polystyrene, providing parts with an excellent balance of toughness and transparency. FEATURES Outstanding toughness High GPPS blend capability Excellent clarity APPLICATIONS Food packaging Food service items Drinking cups Extruded films |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体体积流动速率 Melt Volume Rate |
|||
200℃,5 kg 200℃,5 kg |
12.0 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.070 | % | ISO 62 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
85 | kJ/m² | ISO 179 |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
无断裂 | ISO 179 | |
23℃ 23℃ |
无断裂 | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
ASTM D256 , ISO 180/A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
550 nm 550 nm |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
ISO 868 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ISO 178 | |
5% 应变 5% strain |
MPa |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
朗盛建造新的高功能资料生产工厂
2019-01-02 朗盛 的子公司Bond Laminates GmbH正在增加Tepex品牌连续纤维增强热塑性复合材料的生产能力。 朗盛 目前正在其Brilon工厂新建一个约1500平方米的第四生产中心。 另外两条生产线计划在2019年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |