| 牌号简介 About |
|---|
| Lexan Exl1414树脂Lexan Exl1414聚碳酸酯（PC）硅氧烷共聚物树脂是一种中等流动性不透明注塑（IM）级树脂。与标准PC相比，该树脂具有极低的温度（-40 C）延展性，同时具有良好的加工性和释放性，有机会缩短IM循环时间。LEXAN™ EXL1414 resin是一种可用于各种不透明颜色的产品，可能是多种应用的最佳选择。 LEXAN EXL1414 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade. This resin offers extreme low temperature (-40 C) ductility in combination with excellent processability and release with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1414 resin is a product available in wide range of opaque colors and may be an excellent candidate for a wide variety of applications. |
产品描述 Product Description
厂家：沙特沙伯基础 SABIC
类别：PC Polycarbonate
用途：通用;
颜色：可用颜色,不透明
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 含脱模剂; 成型周期快; 共聚物; 流动性中等; 机械强度好-延展; 易加工; Excellent Processability,Ductility,Quick molding cycle,Good stripping performance,Moderate liquidity,Copolymer,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.18 | g/cm³ | ASTM D792 |
|
密度 Density |
1.19 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
10 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
9.00 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
TD：3.2 mm TD：3.2 mm |
0.40 to 0.80 | % | 内部方法 |
|
MD：3.2 mm MD：3.2 mm |
% | 内部方法 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
|
-30℃ -30℃ |
ISO 180/1U | ||
|
23℃ 23℃ |
ISO 180/1U | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 9 |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，100 mm跨距 1.8 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Ae | |
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，100 mm跨距 0.45 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Be | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
球压测试 Ball pressure test |
|||
|
125℃ 125℃ |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：23~80℃ TD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
MD：23~80℃ MD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
0.8 mm，在油中 0.8 mm in oil |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
0.40 mm 0.40 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
|
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
|
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
|
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
|
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength 3 |
|||
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 3 |
|||
|
断裂 fracture |
% | ISO 527-2/50 | |
|
断裂 fracture 4 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
|
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
|||
|
屈服，50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
L 级 Level L |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.051 in/min |
| 5 0.079 in/min |
| 6 Yield |
| 7 80*10*3 sp=62mm |
| 8 80*10*3 |
| 9 120*10*4 mm |
| 10 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
以疫之名，华东高压行涨价之实
2022-04-13 3月以来，国内本土疫情已经在多地蔓延，尤其是吉林、上海、广东、福建等地，每日新增确诊、无症状感染者数量较多。国内多地收紧防疫措施，国内物流运输大受影响。塑料市场也正 |
||||||||||||||||||||||||||||||||||||
|
以疫之名，华东高压行涨价之实 3月以来，国内本土疫情已经在多地蔓延，尤其是吉林、上海、广东、福建等地，每日新增确诊、无症状感染者数量较多。国内多地收紧防疫措施，国内物流运输大受影响。塑料市场也正面临着较大的挑战。近期监测发现，华东高压料脱颖而出，价格走出了“六亲不认”的步伐，一路高歌，本周塑城上海石化Q281市场价触及14600元/吨，而去年同期为12000元/吨左右，同比涨幅高达217%。
表1 近期华东区域高压价格涨跌表（元/吨） 在此，我们主要解读一下华东区域的高压为何如此强势？ 一、上海疫情严峻，全域实施全封闭管控，上海石化、上海赛科、上海金菲聚乙烯生产企业的货物难以外运。此外物流运输受限制，3月至目前，上海整车货运物流指数从最高的144.52下降到16.45，环比大幅下降88.6%，部分地区对货运司机出台了很严格的管控政策，针对中高风险地区除了需要提供48小时的核酸证明，还需要提前申请电子凭证，所以导致了货运司机需要在货运途中不断进行核酸检测，整体运力大幅下降。江浙地区出台了关停部分高速收费站的情况，导致许多货运车辆被困在高速，整体物流成本再次急剧上升。上海石化高压品种在华东地区有较大的需求，高压价格应声上涨。 二、高压品种的进口依存度最高在56.4%，上海港作为全国重要港口，由于公共卫生事件影响，货物无法靠港，导致高压货源供应偏紧。 三、华东区域高压产能共170万吨，占华东区域聚乙烯总产能的22.2%。正常生产高压产品仅有上海石化和扬子巴斯夫40万吨，其他均生产EVA为主。而浙石化二期4月初刚刚投产，货源未大量流入市场，对市场冲击有限。华东作为高压最大的消费市场，消费类型主要以包装膜、农膜、电缆、注塑领域为主，区域内上海石化、扬子巴斯夫的企业产量多以本地区消耗为主。今年由于受疫情影响，食品药品包装及防疫物资需求增加，高压薄膜、涂覆等领域需求量明显增加。 综上所述，华东区域高压主要受公共卫生事件影响货源偏紧，导致一路走高。后期随着部分地区运输陆续恢复，新投产的高压装置逐步进入市场，华东区域供应会明显增加。届时，价格有高位回落预期。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
原厂数据及认证：
抱歉！该牌号暂无认证数据。
价格走势图
开始时间：
结束时间：
材料厂家：
【牌号齐全，内容全面】
全网共2500+项牌号+上游原料单体+原油价格，最长可追溯近20年价格行情
【精准，及时，权威！】
专业团队挖掘行情信息，第一时间发布行情
抱歉！该牌号暂无认证数据。
免责声明：参考价格是搜料网根据网络大数据拟合分析的结果，仅供参考。实际成交价取决但不限于以下因素：下单时间，付款方式，交货方式，数量，税费，色号，产地，项目信息。
- 对讲机外壳
- 2019-01-25 0
- LEXAN™ EXL1414 resin聚碳酸酯（PC）硅氧烷共聚物树脂是一种中等流动性不透明注塑（IM）级树脂。与标准PC相比，该树脂具有极低的温度（-40 C）延展性，同时具有良好的加工性和释放性，有机会缩短IM循环时间。
- 阅读全文
对讲机外壳
1-LEXAN™ EXL1414 resin聚碳酸酯（PC）硅氧烷共聚物树脂是一种中等流动性不透明注塑（IM）级树脂
2-收缩率（TD：3.2 mm） 0.40-0.80 %
3-弯曲模量（50 mm跨距） 2250 MPa
4-简支梁无缺口冲击强度（ -30℃） 无断裂
5-热变形温度（1.8 MPa，未退火，3.2 mm） 124 ℃
2-收缩率（TD：3.2 mm） 0.40-0.80 %
3-弯曲模量（50 mm跨距） 2250 MPa
4-简支梁无缺口冲击强度（ -30℃） 无断裂
5-热变形温度（1.8 MPa，未退火，3.2 mm） 124 ℃