牌号简介 About |
---|
控制型OTR系列滑动改性双向拉伸聚丙烯薄膜非热封食品包装单侧处理 Controlled OTR Range Slip Modified BIAXIALLY ORIENTED POLYPROPYLENE FILM NON-HEAT SEALABLE, ONE SIDE TREATED FOR FOOD PACKAGING |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
尺寸稳定性 dimensional stability 2 |
|||
TD,130℃ TD,130℃ |
< 3.0 | % | |
MD,130℃ MD,130℃ |
< 5.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
动态 dynamic |
0.20 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
19 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
138 | MPa | ASTM D882 |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
氧气传输速率 Oxygen transfer rate |
|||
22℃,0% RH 22℃,0% RH |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
38℃,90% RH 38℃,90% RH |
g/m²/24 hr | ASTM F1249 | |
用量 dosage 3 |
m²/kg | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面能 Surface energy 4 |
dyne/cm | ASTM D2578 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5 minutes |
3 Internal Method |
4 High Energy Flame Side |
【新闻资讯】查看全部
无模浇注型聚氨酯预聚面子世
2018-08-20 上海鹤城高分子科技有限公司在第十六届中国国际聚氨酯展览(PU China 2018)中展出了一款最新推出的无模浇注型聚氨酯预聚体。 该公司专门生产浇注型聚氨酯预聚体、聚氨酯组合料、聚氨酯粘合剂、和聚氨酯助剂。 总经理董雨磊表示,新产品在20分钟内就能固化,而中国的行业平均水平是1小时。他还表示:预聚物比其他材料具有更高的粘度,但用它生产的零部件具有更好的机械性能和更长的使用寿命。 董还表示,这种新材料还要求优质的机器。他接着补充说,一些少数中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |