牌号简介 About |
---|
SC-89可作为织物、乳胶、泡沫、橡胶和聚氨酯弹性体如S皮FLUX的拉伸涂层。SC-89系列是一种完全反应、不发黄的弹性聚氨酯涂层,通过溶剂蒸发干燥。 SC-89 can be used as a stretch coating for fabrics, latex, foam, rubber, and polyurethane elastomers such as SkinFlex. The SC-89 Series is a fully reacted, non-yellowing elastomeric urethane coating which dries by solvent evaporation. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.910 | g/cm³ | ASTM D792 |
粘度 viscosity |
1.85 | Pa·s | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服 yield |
46.2 | MPa | ASTM D412 |
100% 应变 100% strain |
3.86 | MPa | ASTM D412 |
300% 应变 300% strain |
8.96 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
-- -- 2 |
kN/m | ASTM D624 | |
开裂 cracking |
kN/m | ASTM D470 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
贮藏期限 Storage period |
wk | ||
干燥时间 drying time 3 |
|||
25℃,76.2 µm 25℃,76.2 µm |
min | ||
66℃,76.2 µm 66℃,76.2 µm |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐酸性 Acid resistance |
|||
-- -- 4 |
|||
-- -- 5 |
|||
5% Acidic 5% Acidic |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 wet film on glass |
4 5% Phosphoric |
5 5% Hydrochloric |
【新闻资讯】查看全部
中国新资料产业大而不强 三大难题待解
2016-09-18 日前,以“发展与创新”为主题的2016中国・南京新材料资本技术峰会召开。此次峰会由南京市人民政府主办,600余位与会专家聚焦新材料行业“发展与创新”形势,针对当前新材料行业面临的大而不强等问题,为行业健康发展和引入资本建言献策。 “十三五”规划出台使新材料行业迎来重要的发展契机。国家制造强国建设战略咨询委员会认为,新材料领域产业前景良好,到“十三五”末市场规模将达万亿元。而石墨烯、3D打印、超导等前沿材料的快速发展,则有望在未来继续催生出千亿级市场空间。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |