牌号简介 About |
---|
Telcar Telc-340是为消费者和工业市场设计的通用热塑性弹性体。TELCAR TELC-340是一种高硬度、低密度等级的产品,适用于挤出和注塑成型。 LEXAN ML6413 resin is an impact modified, flame retardant polycarbonate grade with Br- & Cl-free FR systems. It features improved light shielding capability with good flow, impact and thermal properties suitable for various applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,5.0kg 260℃,5.0kg |
24 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
20.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.40 to 0.80 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 7 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 8 |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 8 |
℃ | ISO 75-2/Ae | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 8 |
℃ | ISO 75-2/Be | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 9 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
2.00 mm 2.00 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 A |
3 Instant |
【新闻资讯】查看全部
商务部:2021年全国实际使用外资金额再创历史新高
2022-01-14 搜料网资讯: 在1月13日商务部召开的例行新闻发布会上,商务部新闻发言人束珏婷介绍,2021年全年,全国实际使用外资金额11493.6亿元人民币,同比增长14.9%(折合1734.8亿美元,同比增长 |
商务部:2021年全国实际使用外资金额再创历史新高 搜料网资讯:在1月13日商务部召开的例行新闻发布会上,商务部新闻发言人束珏婷介绍,2021年全年,全国实际使用外资金额11493.6亿元人民币,同比增长14.9%(折合1734.8亿美元,同比增长20.2%;不含银行、证券、保险领域,下同),引资规模再创历史新高。 从行业看,高技术产业和服务业引资增长较快,高技术产业实际使用外资同比增长17.1%,其中高技术制造业增长10.7%,高技术服务业增长19.2%。服务业实际使用外资金额9064.9亿元人民币,同比增长16.7%。 从来源地看,“一带一路”沿线国家和东盟投资增长较快,实际投资同比分别增长29.4%和29%(含通过自由港投资数据),高于全国引资增速。 从区域分布看,我国东部、中部、西部地区实际使用外资同比分别增长14.6%、20.5%和14.2%。 2021年12月27日,国家发展改革委、商务部发布了《外商投资准入特别管理措施(负面清单)(2021年版)》和《自由贸易试验区外商投资准入特别管理措施(负面清单)(2021年版)》,与2020年版相比,2021年版全国和自贸试验区负面清单进一步缩减至31条、27条。 束珏婷指出,2022年,商务部将围绕“稳住外贸外资基本盘”,推动稳总量、优结构、提质量,更加积极有效利用外资,重点开展以下几方面工作: 一是进一步扩大高水平对外开放。落实好2021年版全国和自贸试验区外资准入负面清单,督促加快配套法规文件“立改废”,保障“非禁即入”。修订扩大《鼓励外商投资产业目录》,引导外资更多投向先进制造、现代服务、高新技术、节能环保、绿色低碳、数字经济等新兴领域和中西部地区。 二是进一步推动开放平台建设。建设好自由贸易港、自贸试验区、国家级经开区、服务业扩大开放综合示范试点地区等平台,发挥营商环境和制度型开放优势,吸引更多外资项目落地。办好进博会、广交会、服贸会、消博会、投洽会等重大经贸展会,加大招商引资力度。 三是进一步加强外资企业和项目服务保障。发挥外贸外资协调机制及其重点外资项目工作专班作用,完善重点外资企业和项目“直通车”一对一跟踪服务机制,推动协调解决人员入境等企业关切的问题。会同有关部门加大新项目要素保障力度,推动项目加快落地和建设。 四是进一步优化外商投资环境。全面清理与外商投资法及其实施条例不符的规定,落实外资企业公平待遇。充分发挥外资企业投诉工作机制作用,加大外商投资合法权益保护力度,稳定外国投资者对华投资预期和信心。商务部将继续致力于打造市场化、法治化、国际化的营商环境,使中国长期成为外商投资的热土。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。