牌号简介 About |
---|
PPE + PS共混物。17%矿物增强。无溴、无氯FR系统。UL94 V0和5VA列表。UL76C F1。辐射板列表。介电强度。尺寸稳定性。适用于电气/电子市场室内/室外应用,包括电气天花板盒和烟雾探测器。 PPE+PS blend. 17% Mineral reinforced. Non-brominated, non-chlorinated FR system. UL94 V0 and 5VA listing. UL746C f1. Radiant panel listing. Dielectric strength. Dimensional stability. Suitable for E/E market indoor/outdoor applications including electrical ceiling boxes and smoke detectors. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PPO(PPE)+PS PPO(PPE)+PS
用途:室外应用;电气/电子应用领域;
加工条件:注射成型 Injection Molding
性能特点: 无卤; 防火阻燃等级V-0; 尺寸稳定性好; 阻燃; 防火阻燃等级5VA; Good Dimensional Stability,Halogen free,Flame Characteristics,V-0,5VA
填料:矿物 17
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
280℃,5.0kg 280℃,5.0kg |
7.6 | g/10min | |
300℃,5.0kg 300℃,5.0kg |
7.6 | g/10min | |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
280℃,5 kg 280℃,5 kg |
6.80 | cm³/10min | |
300℃,5 kg 300℃,5 kg |
6.80 | cm³/10min | |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
耐候性 Weathering resistance |
UL 746C | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
100 mm跨距 100 mm span 5 |
MPa | ASTM D790 | |
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ISO 178 | |
屈服,100 mm跨度 Yield, 100 mm span 7 |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span 8 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Be | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 11 |
℃ | ISO 75-2/Ae | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ||
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
|||
60 Hz 60 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
|||
60 Hz 60 Hz |
|||
1 MHz 1 MHz |
|||
耐电弧性 Arc resistance 12 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.47 mm 1.47 mm |
|||
2.01 mm 2.01 mm |
|||
辐射板 Listing(UL) Radiation Plate Listing (UL) |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 0.10 in/min |
5 0.051 in/min |
6 80*10*4 |
7 120*10*4 mm |
8 钨电极 |
【新闻资讯】查看全部
宁波北仑1天新增13例,已提级临时性全域静默管理!
2022-10-17 扫描上图二维码,可以免费下载 搜料 APP 中国第二大、全球第三大集装箱港宁波舟山港核心港区所在地--宁波北仑再次出现新冠确诊病例。 10月16日0-19时,宁波市北仑区新增12例确诊病例 |
宁波北仑1天新增13例,已提级临时性全域静默管理! 中国第二大、全球第三大集装箱港宁波舟山港核心港区所在地--宁波北仑再次出现新冠确诊病例。10月16日0-19时,宁波市北仑区新增12例确诊病例、1例无症状感染者,从13日开始发现1例,到现在北仑每日都有新增。 16日中午12时,北仑发布《关于提级临时性全域静默管理的通告》,报告提出由于全区疫情形势严峻复杂。为彻底切断传播链,决定于10月16日13时起提级临时性全域静默管理。 其中要求达不到封闭式管理条件要求的,暂停生产经营。其他工业和商贸企业暂停生产经营活动。建筑工地暂停施工,仓储物流企业暂停经营。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
原厂数据及认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- NORYL树脂光伏接线盒
- 2022-10-18 0
- NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度,长期在户外的湿热环境使用后,还可保持85%以上的性能,且具有低翘曲特性,满足对接线盒材料的高要求
- 阅读全文
NORYL树脂光伏接线盒
1-NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度;
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
收起
抱歉!暂无数据。