牌号简介 About |
---|
未加固的优异的耐化学性和可涂性。312F(155C)硬盘。 Unreinforced. Excellent chemical resistance and paintability. 312F (155C) HDT. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:130℃,1 hrs MD:130℃,1 hrs |
1.1 到 1.5 | % | ASTM D955 |
MD:3.2 mm MD:3.2 mm |
0.90 到 1.2 | % | 内部方法 |
TD:3.2 mm TD:3.2 mm |
0.80 到 1.1 | % | 内部方法 |
吸水率 Water absorption rate |
ASTM D570 | ||
24hr 24hr |
0.40 | % | ASTM D570 |
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D4812 | ||
-40℃ -40℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-40℃,Energy at Peak Load -40℃,Energy at Peak Load |
J | ASTM D3763 | |
-30℃,Energy at Peak Load -30℃,Energy at Peak Load |
J | ASTM D3763 | |
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 5 | |
-- -- |
℃ | ASTM D1525 6 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-20~150℃ MD:-20~150℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 3 |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
ASTM D638 | ||
屈服 yield |
% | ASTM D638 | |
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
100 mm跨距 100 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
屈服,100 mm跨度 Yield, 100 mm span 4 |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 |
备注 |
---|
3 类型 1, 50 mm/min |
4 2.6 mm/min |
5 标准 B (120°C/h), 载荷2 (50N) |
6 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
东明石化或为一季度唯一出口成品油的山东地炼
2021-05-17 搜料网资讯: 从山东地方炼厂获悉,由于出口效益不及国内销售收入,且农历新年后国内需求好转,山东地方炼厂缺乏出口积极性,一季度预计仅出口成品油1万吨,来自东明石化。 据 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |