牌号简介 About |
---|
透明热塑性聚酰亚胺(TPI)树脂。玻璃化转变温度(Tg)247°C。全球食品接触批准。树脂受美国《商业控制法》第15CFR第七章第774部分和法规附件一的约束。EC 428/2009为ECCN1C008。 Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant and also halogen free according VDE/DIN 472 part 815. Global Food Contact Approvals. Resin is a Dual-use item and is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.30 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
337℃,6.60kg 337℃,6.60kg |
16 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
360℃,5 kg 360℃,5 kg |
8.50 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
内部方法 | ||
MD MD 2 |
0.50 到 0.70 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
0.50 到 0.70 | % | 内部方法 |
TD:3.2 mm TD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 9 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 10 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 10 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ASTM D4812 , ISO 180/1U | ||
-30℃ -30℃ 10 |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 11 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ASTM D1525 12 , ISO 306/B50 12 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~150℃ MD:-40~150℃ |
1/℃ | ASTM E831 | |
MD:23~150℃ MD:23~150℃ |
1/℃ | ISO 11359-2 | |
TD:-40~150℃ TD:-40~150℃ |
1/℃ | ASTM E831 | |
TD:23~150℃ TD:23~150℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 kHz 1 kHz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
-- -- 3 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 4 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
-- -- 6 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 6 , 7 |
MPa | ISO 178 | |
屈服,100 mm跨度 Yield, 100 mm span 8 |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span 5 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 0.20 in/min |
4 类型 1, 0.20 in/min |
5 0.051 in/min |
6 0.079 in/min |
7 Yield |
8 0.10 in/min |
9 80*10*4 sp=62mm |
10 80*10*4 |
11 80*10*4 mm |
12 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
联泓新科位列2021中国精细化工百强第26位
2022-05-05 近日,由全国精细化工原料及中间体行业协作组、中国化工情报信息协会、中国化工信息中心联合主办的2021精细化工产业峰会暨中国精细化工百强发布会在线举行。会议发布了2021中国精 |
联泓新科位列2021中国精细化工百强第26位 近日,由全国精细化工原料及中间体行业协作组、中国化工情报信息协会、中国化工信息中心联合主办的“2021精细化工产业峰会暨中国精细化工百强发布会”在线举行。会议发布了“2021中国精细化工百强”榜单,联泓新材料科技股份有限公司(简称:联泓新科)和龙盛、新和成、万华、东岳等企业入围,联泓新科位列第26位。 会议指出,当前,我国新能源、电子化学品等需求快速增长,带动了精细化工行业的快速发展。2021年,中国精细化工市场规模超过5.5万亿元,年复合增长率达8%,预计2027年有望超过11万亿元。 作为始终坚持创新驱动战略和高端化、差异化、精细化布局的新材料企业,联泓新科在高端新材料领域精耕细作,不断提升核心竞争力。2021年,联泓新科业绩再创历史新高,实现营业收入75.81亿元,比上年增长27.81%;归属于上市公司股东的净利润10.91亿元,比上年增长70.24%;EVA、PP、EOD等产品在各细分领域的优势继续巩固和扩大,高毛利产品占比不断提升。 在做优做强现有产业的同时,公司不断扩大新的产业布局,2021年以来规划并实施了10万吨/年锂电材料-碳酸酯联合装置项目、2万吨/年超高分子量聚乙烯和9万吨/年醋酸乙烯联合装置项目、年产20万吨乳酸及 13万吨聚乳酸项目、新能源材料和生物可降解材料一体化项目等多个重点项目。 10万吨/年锂电材料-碳酸酯联合装置项目 被纳入2022年山东省重大项目名单,已完成建设项目设立安全评价、环境影响评价,项目节能报告已获山东省发展和改革委员会批复,计划于2022年底前建成中交。 2万吨/年超高分子量聚乙烯和9万吨/年醋酸乙烯联合装置项目 已完成建设项目设立安全评价,项目节能报告已获山东省发展和改革委员会批复,计划于2023年上半年建成中交。 年产20万吨乳酸及13万吨聚乳酸项目 入选江西省“5020”重点项目,已完成项目安全预评价,项目节能报告已获江西省发展和改革委员会批复,一期项目计划于 2023 年底前建成投产。 新能源材料和生物可降解材料一体化项目 被纳入2022年山东省重大项目名单,已完成立项,计划于2024-2025年陆续投产。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
- 共封装光学元件
- 2022-12-07 0
- EXTEM™RH1016UCL树脂是一种近红外透明热塑性树脂,其玻璃化转变温度为280°C。这种可注塑树脂可以产生复杂的光学透镜组件,同时在260°C峰值温度焊料回流组件期间保持尺寸稳定性。
- 阅读全文
共封装光学元件
2-能在回流焊工艺之后保持部件的尺寸稳定性
3-具有高产出率的精密微注塑能力
4-强大的光学设计自由度
5-突破性的耐高温性能
6-出色的流动性
7-高折射率和近红外透明性
抱歉!暂无数据。