| 牌号简介 About |
|---|
| NANCAR® 1072是一种具有中高耐油性的羧基改性丁腈橡胶。它可以像普通丁腈橡胶一样加工，只是在混合循环结束时添加了金属氧化物。NANCAR® 1072具有优异的耐磨性和耐磨性。建议用于皮带、工业滚筒、车轮、鞋底、鞋跟和其他需要高耐磨性的机械产品。 NANCAR® 1072 is a carboxyl-modified nitrile rubber with medium-high oil resistance. It may be processed like normal nitrile rubber except that metal oxide is added at the end of the mixing cycle. NANCAR® 1072 offers outstanding abrasion and wear resistance. It is recommended for use in belts, industrial rollers, wheels, shoe soles, heels and other mechanical goods requiring high abrasion resistance. |
产品描述 Product Description
用途：鞋类;传送带修补;滚轴;车轮;
性能特点： 耐磨; 耐油; Good wear resistance,Grease resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.980 | g/cm³ | |
|
门尼粘度 Mooney viscosity |
|||
|
ML 1+4，100℃ ML 1+4，100℃ |
48 | MU | ASTM D1646 |
|
丙烯腈含量（Bound） Acrylonitrile content (Bound) |
26.5 | % | 内部方法 |
|
Stabilizer Stabilizer |
Non-staining | ||
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength 4 |
|||
|
屈服 yield 2 |
25.0 | MPa | ASTM D412 |
|
300% 应变 300% strain 4 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain 4 |
|||
|
断裂 fracture 4 |
% | ASTM D412 | |
|
撕裂强度 tear strength 5 , 2 |
kN/m | ASTM D624 | |
|
压缩形变 Compression deformation 2 |
|||
|
100℃，70 hr 100℃，70 hr 2 |
% | ASTM D395 | |
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
空气中拉伸强度的变化率 The rate of change in tensile strength in air 2 |
|||
|
100℃，70 hr 100℃，70 hr 2 |
% | ASTM D865 | |
|
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 2 |
|||
|
100℃，70 hr 100℃，70 hr 2 |
% | ASTM D865 | |
|
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 2 |
|||
|
邵氏 A，100℃，70 hr Shore A, 100 ℃, 70 hr 2 |
ASTM D865 | ||
|
拉伸强度的变化率 The rate of change in tensile strength 2 |
ASTM D471 | ||
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
|
极限伸长率的变化率 Change rate of ultimate elongation 2 |
ASTM D471 | ||
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
|
邵氏硬度的变化率 The rate of change in Shore hardness 2 |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在ASTM #3油中 Support A, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
|
体积变化 Volume change 2 |
ASTM D471 | ||
|
100℃，70 hr，ASTM 标准油（1号） 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
|
100℃，70 hr，ASTM 标准油（3号） 100 ℃, 70 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热损耗 Heat loss |
% | ASTM D5688 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 friction coefficient |
|||
|
NBS test NBS test |
ASTM D1630 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness 2 |
|||
|
邵氏 A Shaw's A 2 |
ASTM D2240 | ||
|
Abrasion（Test，c.c） Abrasion（Test，c.c） 3 |
DIN 53516 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 (Load weight: 10 NT) |
| 3 硫化 15.0 min 在 320°F |
| 4 Cured for 15.0 min at 160°C |
| 5 C 模具 |
|