牌号简介 About |
---|
AOC的VIPEL F701系列树脂是高分子量、两级间苯二甲酸、不饱和聚酯树脂,具有通用树脂的润湿、固化和加工特性。他们有极好的保质期,是理想的纤维缠绕和喷涂的材料。下面列出了一些选定的树脂,包括高粘度基树脂VIPEL F701-FHG-00。优点耐腐蚀AOC的Vipel F701系列树脂在与无机和有机酸接触时具有优异的耐腐蚀性。许多石油产品,如煤油、加热油和原油,都具有耐溶剂性。请参阅AOC的“耐腐蚀树脂指南”,了解耐腐蚀信息或有关树脂适用于任何特定化学环境的问题,请联系AOC。用途广泛,适用于手工制作、喷涂、纤维缠绕等多种制造方法。 AOC's Vipel F701 Series resins are high molecular weight, two-stage isophthalic, unsaturated polyester resin with the wet out, cure and handling characteristics of general purpose resins. They have an excellent shelf life and are ideal for filament winding and spray-up. A few selected resins are listed below including the high viscosity base resin, Vipel F701-FHG-00. BENEFITS Corrosion resistance AOC's Vipel F701 series resins provide excellent corrosion resistance when used in contact with inorganic and organic acids. Solvent resistance is field-proven for many petroleum products such as kerosene, heating oil and crude oils. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up and filament winding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
48 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
107 | ℃ | ASTM D648 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
10.0 | min | |
放热峰值 exothermic peak |
199 | ℃ | |
触变指数 Thixotropic index 2 |
2.50 | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 LV Brookfield LV |
Pa·s | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2/20 rpm |
【新闻资讯】查看全部
塑料助剂在制品中的运用大全
2017-09-12 有些塑料本身就是单纯的树脂,如聚乙烯、聚苯乙烯等,称为单一组分塑料。有些塑料除了合成树脂之外,还含有其他辅助材料,如增塑剂、稳定剂、着色剂、各种填料等,称为多组分塑料。 塑料助剂在塑料中加入助剂的目的主要是为了改善加工性能,提高使用效能和降低成本。助剂在塑料用料中所占比例较少,但对塑料制品的质量却有很大影响 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |