牌号简介 About |
---|
SUMIKASUPER LCP是一种热致液晶聚酯,在工程塑料中表现出最高的耐热性。 SUMIKASUPER® LCP E6808LHF is a Liquid Crystal Polymer (LCP) material filled with glassinorganic. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of SUMIKASUPER® LCP E6808LHF are: Flame Rated Good Processability Warp Resistant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.70 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
内部方法 | ||
MD MD |
0.17 | % | 内部方法 |
TD TD |
0.40 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和 saturated |
0.020 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
6.4mm 6.4mm |
96 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
6.4 mm 6.4 mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
内部方法 | ||
MD:150℃ MD:150℃ |
1/℃ | 内部方法 | |
TD:150℃ TD:150℃ |
1/℃ | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
1.00 GHz 1.00 GHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
1 GHz 1 GHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.30 mm,本色,黑色 0.30 mm, natural color, black |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | JIS K7201 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Soldering Resistance Soldering Resistance |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
剪切强度 shear strength |
MPa | ASTM D732 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
苹果数据线有救了?日本研收回全球最坚韧软资料
2017-07-27 北海道大学龚剑萍教授带领的团队研发了一种新材料,它看起来很柔软,但是却和钢铁一样坚韧。事实是,它比碳钢坚硬5倍,同时又兼具了如同橡胶般的弹性。 这种新材料是一种坚硬而可弯曲的网状结构材料。它利用水凝胶(常用于制作隐形眼镜)和玻璃纤维制备得到,也可被认为是纤维增强的新型复合材料。龚剑萍表示,这是迄今为止人类获得的最坚硬软材料。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |