牌号简介 About |
---|
Bayflex® XGT-80是一种用于反应注射成型(RIM)工艺的弹性聚氨酯系统。该体系分为两种液体组分:A组分为改性二苯基甲烷二异氰酸酯(MDI),B组分为聚醚多元醇体系。注:多元醇组分相在静置时分离,使用前必须通过机械方式彻底混合。延长的凝胶时间Bayflex® XGT-80使设备设计者能够灵活地创建可在现有注塑机上成型的大型复杂零件。该树脂具有优良的表面质量和高抗冲击性,可用于农业设备、重型卡车、特种运输和海洋应用。 Bayflex XGT-80 is an elastomeric polyurethane system used in the reaction injection molding (RIM) process. The system is supplied as two liquid components: Component A is a modified diphenylmethane diisocyanate (MDI), and Component B is a polyether polyol system. Note: The polyol component phase-separates upon standing and must be thoroughly mixed via mechanical means prior to use. The extended gel time of Bayflex XGT-80 gives equipment designers the flexibility to create large, complex parts that can be molded on existing injection machinery. The resin's excellent surface quality and high impact resistance make it a candidate for agricultural equipment, heavy-duty trucks, specialty transportation, and marine applications. |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PUR-脂肪族+MDI PUR-脂肪族+MDI
用途:船舶应用;农业应用;
加工条件:反应注射成型 (RIM)
性能特点: 防火阻燃等级HB; 冲击性能好; 表面光泽度好; Good surface appearance,High impact resistance,HB
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 , ASTM D1622 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.80 到 0.90 | % | 内部方法 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength 2 |
|||
3.18 mm 3.18 mm 2 |
110 | kN/m | ASTM D624 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
640 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 3 |
ASTM D3763 | ||
-30℃,3.18 mm -30℃,3.18 mm |
5.42 | J | ASTM D3763 |
23℃,3.18 mm 23℃,3.18 mm |
J | ASTM D3763 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Sag(4 in Overhang,121℃,3.18 mm) Heat Sag(4 in Overhang,121℃,3.18 mm) 6 |
cm | ASTM D3769 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3.18 mm Shaw D, 3.18 mm |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃,3.18 mm -30℃,3.18 mm |
MPa | ASTM D790 | |
23℃,3.18 mm 23℃,3.18 mm |
MPa | ASTM D790 | |
70℃,3.18 mm 70℃,3.18 mm |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components 4 |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period 5 |
|||
32℃ 32℃ 5 |
wk | ||
脱模时间 stripping time |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 7.33 ft/sec |
4 1.05 Index |
5 0.125 in |
6 1 hr |
【新闻资讯】查看全部
澳门明年起禁止进口一次性塑料刀叉勺,可降解塑料除外
2022-09-06 扫描上图二维码,可以免费下载 搜料 APP 9月5日,澳门环境保护局宣布,为确保澳门的环境质量,澳门特别行政区政府已依次实施减塑措施。特区政府在推出发泡胶餐具、不可降解一次 |
澳门明年起禁止进口一次性塑料刀叉勺,可降解塑料除外
9月5日,澳门环境保护局宣布,为确保澳门的环境质量,澳门特别行政区政府已依次实施减塑措施。特区政府在推出发泡胶餐具、不可降解一次性塑料餐饮吸管及饮料搅拌棒的管制措施后,综合分析澳门的实际情况,参考其他地区的经验,并与相关工商会交流意见后,根据经第3/2016号法律修订的第7/2003号法律《对外贸易法》第五条第一款(五)项之规定,通过行政长官第175/2022号指示,禁止进口不可降解一次性塑料刀、叉、 匙,有关行政长官的指示将于2023年1月1日起生效。
为让业界更清楚管制范围及相关具体操作要求,澳门环境保护局日后将举行介绍会向业界作进一步讲解,向业界进一步解释,以确保管制措施有效落实。
上搜料工程塑料超市www.soliao.com,可以直达现货商城,全部商品都是原厂原包真货,24小时发货,全国含税含运费。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。