牌号简介 About |
---|
GAPEX® RPP20EV09HB是一种聚丙烯材料,含有的填充物为20% 玻璃纤维增强材料。 该产品在亚太地区、北美洲、拉丁美洲、欧洲或非洲和中东有供货,。 GAPEX® RPP20EV09HB的主要特性有: 冲击改性 化学耦合 紫外线稳定 This linear low density polyethylene is an ethylene-hexene copolymer tailored for film applications that require: Excellent processing characteristics Exceptional drawdown Use alone or in coextrusions; blends with other polyolefins Good stiffness at thin gauges High amounts of slip agent Typical blown film applications include: Coextrusions Blend component to improve drawdown Thin gauge applications General purpose packaging Typical cast film applications include: Overwrap Coextrusions |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
铸造薄膜 Casting thin film |
0.10 | ASTM D1894 | |
吹塑薄膜 Blown film |
0.70 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:25 µm,吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
228 | MPa | ASTM D882 |
1% 正割,MD:32 µm,铸造薄膜 1% secant, MD: 32 µ m, cast thin film |
MPa | ASTM D882 | |
1% 正割,TD:25 µm,吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
MPa | ASTM D882 | |
1% 正割,TD:32 µm,铸造薄膜 1% secant, TD: 32 µ m, cast thin film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,32 µm,吹塑薄膜 MD, fracture, 32 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,32 µm,吹塑薄膜 TD, fracture, 32 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,32 µm,挤塑薄膜 MD, fracture, 32 µ m, extruded film |
% | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,32 µm,挤塑薄膜 TD, fracture, 32 µ m, extruded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
31.8 µm,铸造薄膜 31.8 µ m, cast thin film |
kN/m | ASTM D1709 | |
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:1.0 µm,吹塑薄膜 MD: 1.0 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
撕裂强度 tear strength 2 |
ASTM D1922 | ||
MD,31.8 µm MD,31.8 µm |
kN/m | ASTM D1922 | |
TD,31.8 µm TD,31.8 µm |
kN/m | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
60°,25.4 µm,吹塑薄膜 60 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
60°,31.8 µm,铸造薄膜 60 °, 31.8 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
ASTM D1003 | ||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 | |
31.8 µm,铸造薄膜 31.8 µ m, cast thin film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
理化所发现苯乙烯在催化下可以与脂肪族醇和酮类反响
2016-03-08 中科院理化所王乃兴研究员课题组发现苯乙烯在催化条件下能够与脂肪族醇和酮类直接发生区域选择性反应,一步合成得到有用的双官能团化复杂产物。 绝大多数有机化合物含有C-H键,对不活泼C-H键进行催化官能化在有机合成化学中意义重大。最近,王乃兴课题组发现了芳基烯烃与脂肪族醇的氧化偶联新反应。在氯化锰和叔丁基过氧化氢的催化下,苯乙烯经与脂肪醇的α-C(sp3)-H键官能团化,一步得到目标产物。经过拓展,发现芳基烯烃与低沸点脂肪族醇都能以中等以上的收率很好地发生该反应。所得到的21个目 |
理化所发现苯乙烯在催化下可以与脂肪族醇和酮类反响 中国科学院理化所王乃兴研究者研究组发觉苯乙烯在催化标准下可以与脂环族纯正酮类立即产生地区可选择性反映,一步生成获得有效的双官能团异构化繁杂物质。 绝大部分有机物带有C-H键,对不开朗C-H键开展催化官能化在有机化学有机化学中实际意义重特大。近期,王乃兴研究组发觉了芳香族环己醇与脂环族醇的氧化偶联反应新反映。在氯化锰和叔丁基双氧水的催化下,苯乙烯经与脂肪醇的α-C(sp3)-H键官能团异构化,一步获得总体目标物质。历经扩展,发觉芳香族环己醇与低熔点脂环族醇都能以中等水平之上的收率非常好地产生该反映。所获得的21个总体目标化学物质,都开展了核磁共振氢谱、碳谱和高分辨质谱的评定。 苯乙烯及化合物与脂肪醇的反映 科学研究发表论文在《Nature》集团公司下的Scientific Reports上:Scientific Reports 2015, 5, 15250. DOi: 10.1038/srep15250. 除此之外,王乃兴研究组还发觉了在铜/锰双催化剂下苯乙烯与酮类的高可选择性空气氧化偶联反应。研究发现在锰催化剂协作铜催化剂下的标准下反映收率对比于单一铜催化剂下有显著的提升,在双催化剂和叔丁基双氧水的存有下,苯乙烯经与酮的C(sp3)-H键官能团异构化,一步获得1,4-二羰基繁杂物质。反映标准柔和,地区可选择性高。该催化管理体系运用到不一样替代的端基芬芳环己醇与酮类化学物质且都可以产生该偶联反应。 苯乙烯及化合物与酮类的反映 所获得的22个总体目标化学物质,都开展了1H NMR、13C NMR和高分辨质谱的评定。科研成果发布在分析化学关键学术期刊 Organic Letters 上:Org. Lett., 2015, 17, 4460. DOI: 10.1021/acs.orglett. 5b02116. 来源于:中科院物理化学技术性研究室网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |