TORZEN® U4630HSL NC01是一种热稳定,润滑成型等级PA66自然色。热稳定系统的设计目的是在高温应用中提供优良的性能保持。U4630HSL还提供黑色。 TORZEN® U4630HSL NC01 is a heat-stabilized, lubricated molding grade PA66 in natural color. The heat stabilizer system has been designed to provide excellent property retention in high temperature applications. U4630HSL is also available in black. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:2.0 mm TD:2.0 mm |
2.1 | % | ISO 294-4 |
MD:2.0 mm MD:2.0 mm |
2.1 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
1.7 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3000 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
ISO 179 | ||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
2 mm 2 mm |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
1 mm 1 mm |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.00 mm 3.00 mm |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.40 mm 0.40 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.71 mm 0.71 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.71 mm 0.71 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中策集团打造亚洲规模最大非公路轮胎生产工厂
2022-04-06 4月3日,由中策橡胶集团股份有限公司在天津港保税区注册成立的中策橡胶(天津)有限公司正式开业,中策(天津)高端绿色轮胎制造产业链项目开始投入运营。这是中策集团布局北 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |