| 牌号简介 About |
|---|
| Amodel HFFR-4133 是一种33％玻纤增强、无卤、阻燃聚邻苯二甲酰胺（PPA）树脂，改善了电气和电子产品的加工性能。美国保险商实验室的UL94测试将该树脂定为V-0级，可用温水成型。流动性高、工艺窗口宽、表面外观好，特别是较大的电气元件。 该牌号可耐受电子行业常用的苛刻的红外线回流焊接工艺。非常适用于连接器和其它需要表面贴装技术（SMT）的电气设备。 黑色： HFFR-4133 BK 324 黑色：HFFR-4133 BK 318 本色：HFFR-4133 NT Amodel® HFFR-4133 is a 33% glass-reinforced, halogen-free, flame retardant polyphthalamide (PPA) resin which offers enhanced processing capabilities for electrical and electronic applications. This resin is rated V-0 by Underwriters Laboratories using the UL94 test and is hot-water moldable. It has high flow and a wide processing window and offers good surface appearance, especially for larger electrical components. This grade can withstand the demanding infrared reflow soldering process typically used in the electronics industry. It is well suited for connectors and other electrical devices requiring surface mount technology (SMT). Black: HFFR-4133 BK 324 Natural: HFFR-4133 NT |
产品描述 Product Description
用途：电气/电子应用领域;连接器;
颜色：黑色,自然色
加工条件：水温模具注塑成型
性能特点： 无卤; 防火阻燃等级V-0; 机械强度好; 尺寸稳定性好; 成型周期快; 耐化学性; 阻燃; 电气性好; 韧性好; Good Rigidity,Good flexibility,Good Dimensional Stability,Good Electrical Properties,Quick molding cycle,Halogen free,Flame Characteristics,Solvent resistance,V-0
填料：玻璃纤维 33
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.46 | g/cm³ | ISO 1183/A |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
1.3 | % | ISO 294-4 |
|
MD MD |
0.32 | % | ISO 294-4 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.28 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
7.0 到 8.0 | kJ/m² | ISO 180-1A |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 3 |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
|
MD：0~90℃ MD：0~90℃ |
1/℃ | ASTM E831 | |
|
MD：120~200℃ MD：120~200℃ |
1/℃ | ASTM E831 | |
|
TD：0~90℃ TD：0~90℃ |
1/℃ | ASTM E831 | |
|
TD：120~200℃ TD：120~200℃ |
1/℃ | ASTM E831 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity 4 |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
ASTM D149 | ||
|
0.8 mm 0.8 mm |
kV/mm | ASTM D149 | |
|
1.6 mm 1.6 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
0.40 mm，Black，Natural 0.40 mm，Black，Natural 5 |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength 3 |
|||
|
屈服 yield 3 |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain 3 |
|||
|
断裂 fracture 3 |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength 3 |
MPa | ISO 178 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 本色及BK324色数值高 |
| 3 样本状态：95°F (35°C) ， 90% RH 条件下，放置96 小时 |
| 4 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
|
【新闻资讯】查看全部 
投资逾5亿欧元 巴斯夫扩大环氧乙烷及其衍生物产能
2021-04-21 搜料网资讯： 巴斯夫官网消息，根据公司发展战略，巴斯夫将大幅扩大比利时安特卫普一体化基地的环氧乙烷及其衍生产品的产能。预计总投资将超过5亿欧元，可使相关产品的产能增加 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付