牌号简介 About |
---|
AvaSpire® AV-848 GF30是一种30%的玻璃纤维增强高温聚芳醚酮(PAEK),经过特殊配制,与同等等级的增强型PEEK相比具有多个性能优势。这些措施包括提高尺寸稳定性、提高刚度和将CLTE从150°C降低到240°C,以及降低模量以提高室温下的灵活性。高温AV-848GF30为设计工程师提供了增强PEEK的替代方案,特别是在要求高韧性、更高结构完整性和特殊耐化学性的应用中。使用标准的热塑性熔融加工技术,包括注射成型和挤压,可以很容易地加工出阿凡斯比PAEK。天然:Avaspire AV-848 NT AvaSpire® AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of reinforced PEEK. These include improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. High temperature AV-848 GF30 provides design engineers with an alternative to reinforced PEEK, specifically in demanding applications that require superior toughness, higher structural integrity, and exceptional chemical resistance. AvaSpire® PAEK can be easily processed using standard thermoplastic melt processing techniques, including injection molding and extrusion. Natural: AvaSpire® AV-848 NT |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 3 |
10600 | MPa | ASTM D638 |
拉伸强度 tensile strength 3 |
168 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 3 |
2.3 | % | ASTM D638 |
弯曲模量 Bending modulus |
9900 | MPa | ASTM D790 |
弯曲强度 bending strength |
239 | MPa | ASTM D790 |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 4 |
|||
1.8 MPa,退火,3.2 mm 1.8 MPa, annealed, 3.2 mm 4 |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
比热 specific heat |
DSC | ||
50℃ 50℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3 mm 3 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
熔体质量流动速率 Melt Flow Rate |
|||
400℃,2.16kg 400℃,2.16kg |
g/10min | ASTM D1238 | |
收缩率 Shrinkage rate 2 |
ASTM D955 | ||
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃,1000 sec^-1 400℃,1000 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5" x 0.5" x 0.125" bars |
3 0.20 in/min |
4 200°C,2小时 |
【新闻资讯】查看全部
献策发改委:别让“毒塑料”进入再循环
2018-02-01 毒塑料一旦存在,其生产、使用、废弃、再生过程都可能会持续释放出有毒有害物。 国家发改委公开向社会征求“塑料垃圾污染防治”建言的活动要落下帷幕了,作为环保人士,我也有最后一项个人建议要向发改委提交,即“严格 |
献策发改委:别让“毒塑料”进入再循环 毒塑料一旦存有,其生产制造、应用、废料、再生全过程都很有可能会不断释放出来有毒有害物质。
发改委公布向社会发展征询“塑料垃圾污染治理”建言献策的主题活动要完美收官了,做为环境保护人员,因为我有最终一项本人提议要向国家发改委递交,即“严控塑料有毒化学品加上,严苛管控有毒塑料解决,避免有害物进到再生塑料产品”。 不容置疑,处理塑料垃圾环境污染,不仅在根源减药上采取一定的有效措施,又要根据垃圾分类回收,将能够收购 的废塑料独立搜集起來,从而根据生产加工解决,使其变化为再生塑料及其再生塑料商品。 殊不知,假如一些塑料产品从一开始便是由“毒塑料”生产制造而成的,那麼由他们转换而成的再生塑料,就很可能還是“毒塑料”,相关产品就仍然還是“毒商品”。再向下,假如全部步骤不会改变,“再生毒塑料”还很有可能变为“再再生毒塑料”……这般周而复始,毒塑料会长期地在大家的日常生活存有。 导致毒塑料难题的直接原因有两个。一是一些类型的塑料在一定标准下,自身具有毒性。聚乙烯(PVC)是最典型性的一种,尽管这类人力环氧树脂自身无毒性,但其汇聚原材料氯乙烯单个确是一种已经知道的人们致癌物质。科学研究调研说明,不但一些聚乙烯塑料制成品会出现一定的氯乙烯单个残余,在一些物理学、有机化学标准下,如再生熔化全过程,也会出现较多的氯乙烯单个被释放出。 有心加上有毒化学品是毒塑料存有的另一大缘故。为了更好地让塑料得到 特殊特性,其商品完成特殊作用,塑料制造商会依据必须在原生态塑料中加上各种各样化学品,包含增粘剂、添加剂、填充料、无卤阻燃剂、润滑液这些。而这种防腐剂许多都具备非常高的毒副作用,比如双酚A、酞磷酸盐或酞酸酯、多种多样溴化无卤阻燃剂等。
无论是哪样缘故,毒塑料一旦存有,其生产制造、应用、废料、再生全过程都很有可能会不断释放出来有毒有害物质,造成空气污染,危害大家的身心健康。 上年,一家国际性环境保护组织 公布过一份有关全世界好几个我国少年儿童塑料用具中有毒化学品成分的汇报,結果令人堪忧。在全部试品中,有非常高的占比能够验出浓度较高的的商业八溴二苯醚、十溴二苯醚和六溴环十二烷――这三种已被纳入国际公约关键监管的耐受性有机化学空气污染物。殊不知,据权威专家剖析,这三种化学品都归属于溴化无卤阻燃剂,按相关产品原材料规范的规定,本不应该加上入塑料之中。这表明这种小玩具应用的原材料,很可能是本来就含溴化无卤阻燃剂的废塑料或再生塑料。 更使我们忧虑的是,所述汇报中,在中国销售市场选购的试品一样有非常高的占比可被列入“毒玩具”“毒产品”的范围,产品品种涉及到塑料三阶魔方、塑料雨靴、塑料凉拖、塑料黄小鸭等。 不难看出,塑料垃圾污染治理的重要一环取决于阻拦塑料中有心加上的有毒化学品随塑料再生全过程,进到到新的塑料商品中,及其阻拦塑料在生产加工转换全过程中造成新的有害物。 因此,发改委在制订总体的塑料垃圾污染治理现行政策时,理应优先选择考虑到在根源限定塑料有毒有机化学添加剂的应用,另外规定产品品质单位、环保局对塑料产品或废塑料再生商品的有害物质开展监视系统。另外,也要科学研究颁布有毒塑料无害化处理处理的有关标准规范,进而最大限度地阻隔有害物曝露,让塑料循环系统再生领域真实越来越清理起來。 来源于:新京报网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。