| 牌号简介 About |
|---|
| AvaSpire® AV-848 GF30是一种30%的玻璃纤维增强高温聚芳醚酮（PAEK），经过特殊配制，与同等等级的增强型PEEK相比具有多个性能优势。这些措施包括提高尺寸稳定性、提高刚度和将CLTE从150°C降低到240°C，以及降低模量以提高室温下的灵活性。高温AV-848GF30为设计工程师提供了增强PEEK的替代方案，特别是在要求高韧性、更高结构完整性和特殊耐化学性的应用中。使用标准的热塑性熔融加工技术，包括注射成型和挤压，可以很容易地加工出阿凡斯比PAEK。天然：Avaspire AV-848 NT AvaSpire® AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of reinforced PEEK. These include improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. High temperature AV-848 GF30 provides design engineers with an alternative to reinforced PEEK, specifically in demanding applications that require superior toughness, higher structural integrity, and exceptional chemical resistance. AvaSpire® PAEK can be easily processed using standard thermoplastic melt processing techniques, including injection molding and extrusion. Natural: AvaSpire® AV-848 NT |
产品描述 Product Description
用途：石油/天然气用品;密封件;
颜色：自然色
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 尺寸稳定性好; 耐化学性; 耐疲劳性好; 耐高温; 阻燃; Good Rigidity,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Fatigue resistance,Solvent resistance
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 3 |
10600 | MPa | ASTM D638 |
|
拉伸强度 tensile strength 3 |
168 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain 3 |
|||
|
断裂 fracture 3 |
2.3 | % | ASTM D638 |
|
弯曲模量 Bending modulus |
9900 | MPa | ASTM D790 |
|
弯曲强度 bending strength |
239 | MPa | ASTM D790 |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
MPa | ASTM D732 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 4 |
|||
|
1.8 MPa，退火，3.2 mm 1.8 MPa, annealed, 3.2 mm 4 |
℃ | ASTM D648 | |
|
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
比热 specific heat |
DSC | ||
|
50℃ 50℃ |
J/kg/℃ | DSC | |
|
200℃ 200℃ |
J/kg/℃ | DSC | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
3 mm 3 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ASTM D792 | |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
400℃，2.16kg 400℃，2.16kg |
g/10min | ASTM D1238 | |
|
收缩率 Shrinkage rate 2 |
ASTM D955 | ||
|
MD：3.2 mm MD：3.2 mm |
% | ASTM D955 | |
|
TD：3.2 mm TD：3.2 mm |
% | ASTM D955 | |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
% | ASTM D570 | |
|
熔体表观粘度 Apparent viscosity of melt |
|||
|
400℃，1000 sec^-1 400℃，1000 sec^-1 |
Pa·s | ASTM D3835 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 5" x 0.5" x 0.125" bars |
| 3 0.20 in/min |
| 4 200°C，2小时 |
|
【新闻资讯】查看全部 
全国大部分省份的燃油价格又有微升
2022-04-17 四月一日，加拿大联邦政府再度上调征收的碳排放定价，令近期已经高企的全国大部分省份的燃油价格又有微升。按照加政府二○一九年起执行的碳排放定价制度，当局对油气燃料征收 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付