牌号简介 About |
---|
全石油化工聚丙烯5571是一种高抗冲共聚物,其熔体流动速度为7 g/10 min,其抗冲击性能显著提高,同时具有良好的抗静电性能和加工性能。全聚丙烯5571是专门为篮子,提桶,玩具和任何需要额外韧性的物品的注塑成型开发的。 Polypropylene 5571 is a high impact copolymer with a Melt Flow of 7 g/10min 5571 is characterized by significantly improved impact resistance and good processability. 5571 has been developed specifically for cast film applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
7.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
23.4 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
屈服 yield |
7.0 | % | ASTM D638 |
弯曲模量 Bending modulus |
1170 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-20℃ -20℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
热变形温度 Hot deformation temperature |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
宏昌电子子公司获得发明专利证书
2022-05-24 宏昌电子发布公告称,公司全资子公司珠海宏昌电子材料有限公司于近日收到了国家知识产权局颁发的发明专利证书,发明名称:一种聚苯醚环氧树脂组合物、制备方法和应用。 本专利 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |