牌号简介 About |
---|
纤维素增强苯酚改性三聚氰胺模塑料与MP 181相比,尺寸稳定性和电气性能得到改善,表面硬度优异,机械强度和耐热性好,在电气工程中具有良好的耐磨性和抗紫外线稳定性。该产品满足重金属和PC的允许上限。根据ISO 14529-1:MP(LD20+MD30)-(LD30+MD20)DIN 7708:MP 183,还符合欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)标识的要求。 Cellulose reinforced phenol-modified Melamine moulding compound Improved dimensional stability and electrical properties compared to MP 181, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability Moulded parts in electrical engineering This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) Identification according to ISO 14529-1: MP (LD20 + MD30) - (LD30 + MD20) DIN 7708: MP 183 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.60 到 1.70 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.55 到 0.75 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate |
ISO 2577 | ||
MD MD 3 |
0.70 到 1.1 | % | ISO 2577 |
MD MD 4 |
0.40 到 0.80 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 1.7 | % | ISO 62 |
后收缩 Post contraction 5 |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
注塑成型 injection molding |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
注塑成型 injection molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ISO 178 | |
注塑成型 injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ISO 178 | |
注塑成型 injection molding |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eA | |
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eU | |
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:50~100℃ MD:50~100℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
最高使用温度 Maximum operating temperature |
IEC 60216 | ||
<50 h <50 h |
℃ | IEC 60216 | |
20,000 h 20,000 h |
℃ | IEC 60216 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩成型压力 Compression molding pressure |
MPa | ||
压缩成型温度 Compression molding temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Compression Molded |
3 Injection Molded |
4 168 h / 110°C |
【新闻资讯】查看全部
新华热评:坚决纠正运动式“减碳”
2021-08-07 搜料网资讯: 7月30日召开的中共中央政治局会议提出,要统筹有序做好碳达峰、碳中和工作,尽快出台2030年前碳达峰行动方案,坚持全国一盘棋,纠正运动式减碳,先立后破,坚决遏制 |
新华热评:坚决纠正运动式“减碳” 搜料网资讯:7月30日召开的中共中央政治局会议提出,要统筹有序做好碳达峰、碳中和工作,尽快出台2030年前碳达峰行动方案,坚持全国一盘棋,纠正运动式“减碳”,先立后破,坚决遏制“两高”项目盲目发展。 力争2030年前实现碳达峰、2060年前实现碳中和——我国提出的“双碳”目标彰显了坚定走绿色发展之路的决心,“做好碳达峰、碳中和工作”也被列为“十四五”开局之年的重点任务之一。 实现“双碳”目标,在我国并非易事。在肯定一些地方、企业积极行动的同时,也要看到,有一些地方在空喊口号、蹭热度,还有一些地方有过度行动的倾向,超过了目前的发展阶段。这种运动式“减碳”,一哄而上、缺乏统筹,可能会造成减排成本和效益难以达到最优,甚至可能影响到经济的正常发展。 也有一些地方出现将“碳达峰”曲解为“攀高峰”,认为2030年前还可以继续大幅提高化石能源使用量。近期中央生态环境保护督察就发现,一些地方存在盲目上马“两高”项目的冲动,有“大上、快上、抢上、乱上”的势头。如果任由“两高”项目盲目发展,碳排放增加速率快,碳排放会在一个相当高的水平达峰,造成后期碳中和要承担更大的压力和代价。 我国经济体量大,东中西部经济发展阶段、排放现状、减排潜力有很大差异。一些经济较为发达的城市,服务业比重高,高排放的工业产业转移到其他地区,碳达峰难度相对较小。有些地方承担的经济发展任务不同,产业结构偏重,面临的“减碳”任务更为艰巨。因此,需要全国一盘棋统筹考虑。 实现碳达峰、碳中和是一项复杂、长期和系统性的工程,需要科学部署目标任务、加强顶层设计。不论是地方、行业还是企业,都要合理设置目标,一切从实际出发,科学把握节奏。要处理好发展和减排、整体和局部、短期和中长期的关系,处理好减污降碳和能源安全、产业链供应链安全、粮食安全、群众正常生活的关系。 坚持全国一盘棋,统筹有序、科学“减碳”,我们会打赢碳达峰、碳中和的硬仗。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |