Eltex® PF6112AA是一种在欧洲生产的茂金属LLDPE树脂。其优点和特点是Eltex® PF6112AA是一种含己烯-1的聚乙烯共聚物,它是用茂金属催化剂制备的共聚单体。它是一种非常高韧性的材料,具有以下特性:无与伦比的冲击强度、优异的抗穿刺性能、优异的光学性能、非常好的气泡稳定性和挤出性,类似于最好的LLDPE吹塑薄膜等级、低温密封特性,已开发用于食品包装的应用Eltex® PF6112AA。以及其他需要优异机械和光学性能的薄膜应用。它还特别适用于相对较厚的薄膜应用,需要优越的机械强度和容易密封,如容器和筒仓的内衬。此外,Eltex® PF6112AA提供了容易挤压。在多层膜中,Eltex® PF6112AA可以整齐地使用,也可以作为与LLDPE或LDPE的混合伙伴。 Eltex® PF6112AA is a metallocene LLDPE resin produced in Europe. Benefits and Features Eltex® PF6112AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It is a very high toughness material offering the following properties: Unrivalled impact strength Excellent puncture resistance Superior optical properties Very good bubble stability and extrudability similar to the best LLDPE blown film grades Low temperature sealing characteristics Applications Eltex® PF6112AA has been developed for use in food packaging and other thin film applications where superior mechanical and optical performance is required. It is also particularly suitable for relatively thick film applications requiring superior mechanical strength and easy sealing like liners for containers and silos. In addition, Eltex® PF6112AA offers easy extrudability. In multilayer films, Eltex® PF6112AA can be used neat or as a blending partner with LLDPE or LDPE. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.916 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.3 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
155 | MPa | ISO 527-3 |
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
160 | MPa | ISO 527-3 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
扬子石化停止长玻纤增强聚丙烯公用料工业化生产
2019-01-31 1月17~19日,扬子石化塑料厂采纳扬子研究院的质量改进建议,进行长玻纤增强聚丙烯专用料工业化生产,解决了粒子外观问题,产品性能稳定,质量进一步提升,基本达到国外先进水平。此举标志着中国石化集团公司2018年重大攻关项目――长玻纤增强聚丙烯专用料生产技术取得突破,实现进口替代。 长玻纤增强聚丙烯作为汽车轻量化的重要原料之一,具有高熔指、高模量、性能好的特点,被广泛应用于汽车保险杠、仪表盘等汽车内外构件,可有效实现汽车轻量化,降低油耗。然而,该产品市场长期以来一直都被进口料占 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |