牌号简介 About |
---|
BJ368Mo是一种流动性好、高刚度和高冲击强度的最佳组合的聚丙烯共聚物。采用硼化成核技术对材料进行了成核。流动特性、形核和良好的刚度使循环时间减少。该材料具有良好的抗静电性能和良好的脱模性能。 BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borealis Nucleation Technology (BNT). Flow properties, nucleation and good stiffness give potential for cycle time reduction. The material have good antistatic performance and good mould release properties. Applications Thin wall containers Special Features stiffness and impact balance Good flow behaviour Reduced cycle time and increased output |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
70 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
1500 | MPa | ISO 527-2/50 |
拉伸强度 tensile strength |
|||
屈服 yield |
25.0 | MPa | ISO 527-2/50 |
拉伸应变 Tensile strain |
|||
屈服 yield |
4.0 | % | ISO 527-2/50 |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃ -20℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
℃ | ISO 75-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
建议中止塑料垃圾燃烧的可再生能源补贴 促进回收
2018-02-11 在近日国家发改委为塑料垃圾污染防治公开征集意见中,环保组织零废弃联盟向发改委献策:停止塑料垃圾焚烧的可再生能源补贴。 零废弃联盟创始人毛达表示,现行的生活垃圾焚烧发电补贴标准,将焚烧厂所有入厂垃圾都当成了“生物质能源”给予政策支持。然而,其中也包括大量塑料垃圾,其主要源自于化石能源,不是生物质废物,不可划入可再生能源的范畴。 根据推算,零废弃联盟提出,“有很大部分本来旨在支持生物质可再生能源的电价补贴,错误补到了塑料垃圾焚烧的部分”。 毛达认 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |