牌号简介 About |
---|
产品说明TOPAS® Elastomer E-140与大多数TOPAS等级不同,是一种具有柔韧性的半结晶环状烯烃材料。它是一种相当硬的弹性体,可以挤压和注塑,可以与其他TOPAS等级,其他烯烃树脂和弹性体混合。对于弹性体,E-140具有高防潮性,并且在薄片或薄膜中具有极好的透明度。从E-140特性(如低温脆性)来看,-6°C的二次热失重相对较小。TG主要低于-90°C,而熔点约为84°C。所选应用高韧性薄膜(作为CoC混合物)管袋二次成型食品包装食品接触主要属性韧性、透明度、硬度、低WVTR、可回收性纯度、抗扭结纯度、烯烃相容性、耐冷性、对烯烃的粘附性、纯度不含双酚A、邻苯二甲酸盐或卤素的柔软触感,符合广泛的法规要求。 Product Description TOPAS Elastomer E-140, unlike most TOPAS grades, is a semicrystalline cyclic olefin material with flexibility. It is a fairly stiff elastomer which can be extruded and injection molded, and can be blended with other TOPAS grades, other olefin resins and elastomers. For an elastomer, E-140 features high moisture barrier and has excellent clarity in thin sections or films. Secondary Tg of -6°C is relatively insignificant in terms of E-140 properties such as low temperature brittleness. The major Tg is below -90°C, while the melting point is about 84°C. Selected Applications High toughness film (as COC blend) Tubing Bags Overmolding Food packaging Food contact Leading Attributes Toughness, clarity, stiffness, low WVTR, reclaimability Purity, kink resistance Purity, olefin compatibility, cold resistance Adhesion to olefins, purity, soft feel Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
2.7 | g/10min | ISO 1133 |
260℃,2.16kg 260℃,2.16kg |
11 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
3.00 | cm³/10min | ISO 1133 |
260℃,2.16 kg 260℃,2.16 kg |
12.0 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,0.127 mm Shaw A, 0.127 mm |
ISO 868 | ||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
拉伸模量 Tensile modulus |
ISO 527-3/1 | ||
MD,130 µm,吹塑薄膜 MD, 130 µ m, blow molded film |
MPa | ISO 527-3/1 | |
TD,130 µm,吹塑薄膜 TD, 130 µ m, blow molded film |
MPa | ISO 527-3/1 | |
拉伸强度 tensile strength |
ISO 527-3/50 | ||
MD,断裂,130 µm,吹塑薄膜 MD, fracture, 130 µ m, blow molded film |
MPa | ISO 527-3/50 | |
TD,断裂,130 µm,吹塑薄膜 TD, fracture, 130 µ m, blow molded film |
MPa | ISO 527-3/50 | |
拉伸应变 Tensile strain |
ISO 527-3/50 | ||
MD,断裂,130 µm,吹塑薄膜 MD, fracture, 130 µ m, blow molded film |
% | ISO 527-3/50 | |
TD,断裂,130 µm,吹塑薄膜 TD, fracture, 130 µ m, blow molded film |
% | ISO 527-3/50 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:130 µm,吹塑薄膜 MD: 130 µ m, blow molded film |
g | ASTM D1922 | |
TD:130 µm,吹塑薄膜 TD: 130 µ m, blow molded film |
g | ASTM D1922 | |
透氧率 Oxygen permeability |
|||
23℃,130 µm,吹塑薄膜,50% RH 23 ℃, 130 µ m, blow molded film, 50% RH |
cm³·mm/m²/atm/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
130 µm,23℃,吹塑薄膜,85% RH 130 µ m, 23 ℃, blow molded film, 85% RH |
g·mm/m²/atm/24 hr | DIN 53122 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ISO 974 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
127 mm 127 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant 2 |
|||
0.127 mm,1.00 GHz 0.127 mm,1.00 GHz 2 |
ASTM D2520 | ||
耗散因数 Dissipation factor 2 |
|||
0.127 mm,1.00 GHz 0.127 mm,1.00 GHz 2 |
ASTM D2520 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,127 µm,吹塑薄膜 60 °, 127 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
127 µm,吹塑薄膜 127 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 B |
【新闻资讯】查看全部 |
陶氏泰国新工厂加大硬泡聚醚多元醇消费 11月26日,陶氏化学公司宣布在泰国罗勇新的世界级硬质聚氨酯泡沫多元醇工厂正式投产。新装置将提高公司提供高质量绝缘材料和可靠、节能解决方案的能力,客户和社会都能从中受益。 陶氏聚氨酯业务总裁Jane Palmieri说:“新装置的投产表明了陶氏化学持续投资聚氨酯业务的决心,以便为我们的客户提供符合全球趋势,如人口增长和能源效率的创新解决方案。罗勇工厂是陶氏化学全球聚氨酯生产网络的重要补充,进一步增强了我们提供行业领先产品的能力,帮助客户减少他们的环境足迹,同时在整个产品生命周期带来持久的社会、环境和经济效益。” 聚醚多元醇是聚氨酯硬泡的关键原料,它在建筑保温、冷链和家电中的应用,能够有效保持食品新鲜,防止建筑能源损失。陶氏高性能多元醇使得新的能源效率解决方案成为可能,这帮助客户满足严格的、针对具体国家的法规,同时遵循全球可持续性趋势。 陶氏聚氨酯亚太区商业总监Christina Yu说:“我们生活在一个需要创新和有效的解决方案,来应对紧迫的可持续性挑战的时代,包括能源消耗和气候变化。”在亚太地区,这一点尤其重要,因为人口的大幅增长以及能源消耗的增长正导致对能源效率解决方案的更高需求,而陶氏作为世界领先的材料科学公司,最适合提供能源效率解决方案。 11月8日,来自全球的约150名客户和合作伙伴参加了陶氏化学新多元醇工厂的剪彩仪式。这家新的多元醇工厂加强了陶氏在泰国整合上游工厂的能力,并进一步扩大了道琼斯在亚太地区的影响力。最近,陶氏在印度Lote Parshuram和中国张家港开设了新的聚氨酯系统料工厂。 新多元醇工厂设计年生产能力为7.9万吨,位于罗勇省的亚洲工业园区(AIE),陶氏在AIE有6套生产装置。该工业园区占地515公顷,在经营和管理方面遵循最先进的环境、健康和安全标准,利用尖端技术最大限度地减少其总体环境足迹。 来源:环球聚氨酯网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。