产品说明TOPAS® Elastomer E-140与大多数TOPAS等级不同,是一种具有柔韧性的半结晶环状烯烃材料。它是一种相当硬的弹性体,可以挤压和注塑,可以与其他TOPAS等级,其他烯烃树脂和弹性体混合。对于弹性体,E-140具有高防潮性,并且在薄片或薄膜中具有极好的透明度。从E-140特性(如低温脆性)来看,-6°C的二次热失重相对较小。TG主要低于-90°C,而熔点约为84°C。所选应用高韧性薄膜(作为CoC混合物)管袋二次成型食品包装食品接触主要属性韧性、透明度、硬度、低WVTR、可回收性纯度、抗扭结纯度、烯烃相容性、耐冷性、对烯烃的粘附性、纯度不含双酚A、邻苯二甲酸盐或卤素的柔软触感,符合广泛的法规要求。 Product Description TOPAS Elastomer E-140, unlike most TOPAS grades, is a semicrystalline cyclic olefin material with flexibility. It is a fairly stiff elastomer which can be extruded and injection molded, and can be blended with other TOPAS grades, other olefin resins and elastomers. For an elastomer, E-140 features high moisture barrier and has excellent clarity in thin sections or films. Secondary Tg of -6°C is relatively insignificant in terms of E-140 properties such as low temperature brittleness. The major Tg is below -90°C, while the melting point is about 84°C. Selected Applications High toughness film (as COC blend) Tubing Bags Overmolding Food packaging Food contact Leading Attributes Toughness, clarity, stiffness, low WVTR, reclaimability Purity, kink resistance Purity, olefin compatibility, cold resistance Adhesion to olefins, purity, soft feel Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
2.7 | g/10min | ISO 1133 |
260℃,2.16kg 260℃,2.16kg |
11 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
3.00 | cm³/10min | ISO 1133 |
260℃,2.16 kg 260℃,2.16 kg |
12.0 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,0.127 mm Shaw A, 0.127 mm |
ISO 868 | ||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
拉伸模量 Tensile modulus |
ISO 527-3/1 | ||
MD,130 µm,吹塑薄膜 MD, 130 µ m, blow molded film |
MPa | ISO 527-3/1 | |
TD,130 µm,吹塑薄膜 TD, 130 µ m, blow molded film |
MPa | ISO 527-3/1 | |
拉伸强度 tensile strength |
ISO 527-3/50 | ||
MD,断裂,130 µm,吹塑薄膜 MD, fracture, 130 µ m, blow molded film |
MPa | ISO 527-3/50 | |
TD,断裂,130 µm,吹塑薄膜 TD, fracture, 130 µ m, blow molded film |
MPa | ISO 527-3/50 | |
拉伸应变 Tensile strain |
ISO 527-3/50 | ||
MD,断裂,130 µm,吹塑薄膜 MD, fracture, 130 µ m, blow molded film |
% | ISO 527-3/50 | |
TD,断裂,130 µm,吹塑薄膜 TD, fracture, 130 µ m, blow molded film |
% | ISO 527-3/50 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:130 µm,吹塑薄膜 MD: 130 µ m, blow molded film |
g | ASTM D1922 | |
TD:130 µm,吹塑薄膜 TD: 130 µ m, blow molded film |
g | ASTM D1922 | |
透氧率 Oxygen permeability |
|||
23℃,130 µm,吹塑薄膜,50% RH 23 ℃, 130 µ m, blow molded film, 50% RH |
cm³·mm/m²/atm/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
130 µm,23℃,吹塑薄膜,85% RH 130 µ m, 23 ℃, blow molded film, 85% RH |
g·mm/m²/atm/24 hr | DIN 53122 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ISO 974 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
127 mm 127 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant 2 |
|||
0.127 mm,1.00 GHz 0.127 mm,1.00 GHz 2 |
ASTM D2520 | ||
耗散因数 Dissipation factor 2 |
|||
0.127 mm,1.00 GHz 0.127 mm,1.00 GHz 2 |
ASTM D2520 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,127 µm,吹塑薄膜 60 °, 127 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
127 µm,吹塑薄膜 127 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 B |