牌号简介 About |
---|
Synthos EPS F/PL型0308F、0513F、0816F、1325F为自熄型可膨胀聚苯乙烯EPS,戊烷含量高。这些材料是由球形聚苯乙烯颗粒形成的,这些颗粒含有阻燃系统(HBCD含量<0.5%)和碳氢化合物发泡剂。它们的表面经过处理,以防在加工和静电形成过程中发生粘合。由于卤代阻燃剂和残留发泡剂的含量,本产品不适合直接接触食品的物品。Synthos EPS® 0816F/PL(Owipian FS 0816)主要用于生产中等密度和更高密度的砌块;用于从砌块中切割出的用于隔热的板材和型材,例如建筑物体或包装技术。 Synthos EPS® F /PL type 0308F, 0513F, 0816F and 1325F is self-extinguishing expandable polystyrene EPS with high content of pentane. The materials are formed by spherical polystyrene particles that contain a flame retardant system (content of HBCD < 0,5%) and a hydrocarbon blowing agent. Their surface is treated against gluing during processing and the formation of electrostatic charge. Due to the content of halogenated flame retardant and the residual blowing agent, the product is unsuitable for objects intended for direct contact with food. Synthos EPS® 0816F/PL (Owipian FS 0816) is mainly used for production of blocks with medium and higher density; of cutted boards and profiles from the blocks for a thermal insulation e.g. building objects or in packaging technology. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表观密度 Apparent density |
内部方法 | ||
-- -- 2 |
< 0.02 | g/cm³ | 内部方法 |
-- -- 3 |
0.02 到 0.04 | g/cm³ | 内部方法 |
含水率 Moisture content |
< 7000 | ppm | 内部方法 |
颗粒大小 Particle size |
|||
>95% between >95% between |
0.800 到 1.60 | mm | 内部方法 |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Reaction to Fire Reaction to Fire |
|||
-- -- |
Class E | EN 13501-1 | |
-- -- |
DIN 4102 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blowing Agent Blowing Agent |
wt% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 The laboratory tests of expanded beads bulk density are made according to Polish Standard PN-90/C-89298 using the following expansion times: 0308 and 0513: 12 min., 0816: 10 min., 1325: 6 min. |
3 The typical bulk density indicates values obtained during single-step pre-foaming on continuous pre-foaming devices Lower values of bulk density can be achieved only after multiple pre-expansion. |
【新闻资讯】查看全部
东华能源茂名项目投资1000亿元,首套PP计划2022年末投产!
2022-01-06 搜料网资讯: 2020年3月动工的东华能源茂名烷烃资源综合利用项目,是茂名建市以来引进的最大民营工业项目。 东华能源(茂名)有限公司常务副总经理 孙灿乾:我们东华能源计划在茂 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |