牌号简介 About |
---|
CALIBRE™ IM 401-18 抗冲击改性聚碳酸酯树脂有不透明的配方,其优点涵盖特别优异的低温抗冲击强度和加工简易性,以及其高填充配方所具有的更高的抗冲击强度。 主要特征: 经抗冲击改性 优异的低温韧性 应用领域: 汽车内饰 汽车外饰 小型与大型电器 CALIBRE™ IM 401-18 Impact Modified Polycarbonate resins is available in opaque formulations that offer benefits ranging from superior low temperature impact strength to easy processing with improved impact strength in highly filled formulations. Main Characteristics: Impact modified Superior low temperature toughness Applications: Automotive interiors Automotive exteriors Small & large appliances |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ASTM D792 |
密度 Density |
1.18 | g/cm³ | ISO 1183/B |
密度 Density |
1.19 | g/cm³ | ISO 1183-2 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
18 | g/10min | ASTM D1238 |
300℃,1.20kg 300℃,1.20kg |
18 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
|||
MD MD |
% | ISO 294-4 | |
MD MD |
% | ASTM D955 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 2 | |
拉伸强度 tensile strength 3 |
|||
屈服 yield |
MPa | ISO 527-2 2 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 2 | |
Nominal strain at break Nominal strain at break |
% | ISO 527-2 2 | |
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA 2 | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA 2 | |
简支梁冲击强度 Charpy impact strength |
|||
23℃ 23℃ |
ISO 179/1eU 2 | ||
-30℃ -30℃ |
ISO 179/1eU 2 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ISO 180-4A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 7 |
|||
23℃,Total Energy 23℃,Total Energy 7 |
J | ASTM D3763 | |
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa 1.8 MPa |
℃ | ISO 75-2 2 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-2 2 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 8 | |
B50 B50 |
℃ | ISO 306 | |
B50 B50 |
℃ | ISO 306 2 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 9 |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
阻燃等级 Flame retardant level |
|||
1.60 mm 1.60 mm |
ISO 1210 2 | ||
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
ISO 1210 2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
3 2,0 in/min |
4 方法 I (三点负荷), 0,079 in/min |
5 0,079 in/min |
6 3 点 |
7 11,1 ft/sec |
8 速率 A (50°C/h), 载荷2 (50N) |
9 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
2021年中国乙烯行业市场供给现状及发展前景分析 2025年乙烯产能或将突
2021-09-27 搜料网资讯: 1、十三五时期乙烯产能年均复合增长近10% 2015-2020年,中国乙烯产能从2200.5万吨增长至3518万吨,年均复合增长率近10%。2020年中国乙烯产能达到3518万吨,同比增长14.7%。 2 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |